Electronics Forum | Wed Aug 16 12:07:55 EDT 2017 | ks0707
Reflow -> Wash ? And is there any difference among Leaded / Lead-Free, Water-soluble / No-clean and One-side / Top&Bottom ? If there are any correlations with Wash-process, please send me those information too. Also, if I can get same information f
Electronics Forum | Sat Dec 16 06:16:14 EST 2017 | sherman
In order to find applicable fume extraction, actually it depends on your application. we would like to ask you to check out: http://widaco.net/ to fine out products that we can provide. Fume extraction units that we provide fall into 2 groups: solde
Electronics Forum | Thu Jul 25 18:41:52 EDT 2019 | myke03o
Hi I have solved the issue. The component cracking are the big 1210, 0603 and 0402 capacitors. After studying and testing in many type of solder. The best to use is SnPb and the components are the key - there are component which will tend to expand
Electronics Forum | Thu Sep 05 10:15:58 EDT 2019 | SMTA-Richard
There are multiple solder alloy options and we have tested many of them in a consortium project. There also are very specific challenges associated with testing using the -40/150 C profile. This is way too complicated to discuss in a chat room. Se
Electronics Forum | Thu Sep 05 11:05:35 EDT 2019 | SMTA-Tony
There are competitors to REL solder alloys from AIM. Tin-Copper-Nickel-Bismuth alloys (Nihon Superior) are an alternative option which do very well in thermal cycle testing. The reflow profiles required are similar to SAC305 profiles. You may als
Electronics Forum | Thu Feb 08 08:37:55 EST 2018 | proceng1
We have two Wave Solder machines and still use the FOAMING flux, but the formula we used to use was discontinued, and the one we are currently using isn't as good. I'm hoping that others are still foaming and will share what flux formula they are us
Electronics Forum | Mon Apr 09 11:34:59 EDT 2018 | emeto
definitely don't mix clean and No clean. Run No Clean as you decided, but have your flux and paste manufacturers advice, how this flux can be cleaned(if you decide or required to clean). I know for a fact that some of these NC flux residues are almos
Electronics Forum | Mon Apr 09 09:39:40 EDT 2018 | justconmac
Having an issue with tracking for the Vitronics Soltec Delta 3. Wave will not give error on "expected PCB at exit" but will still show 1+ pcb's in the wave when the machine is empty. This is causing solder pump to idle unnecessarily. Outfeed sensor i
Electronics Forum | Tue Apr 10 08:37:36 EDT 2018 | davef
Hi Steve ... I found nothing in the manufacturers "paper" to help. Comments are: * I agree. No blobs. Solder on the thermal pad should me minimized. Too much solder will float the component. Old timers used to talk about 50-80% coverage. * If you'
Electronics Forum | Wed Apr 18 08:57:45 EDT 2018 | davef
Here is the IPC Standards Tree [ http://www.ipc.org/4.0_Knowledge/4.1_Standards/SpecTree.pdf ]. The design standards that you ask about are over on the right side. I'd guess that the following standards would be a good starting point: * IPC-2221, "
winsouce.jpg)