Electronics Forum | Fri Jul 01 20:02:34 EDT 2005 | Tom B
1st Consider the time involved with upgrading and troubleshooting! Is it worth it? With prices of PC's near to nothing, it may prove cheaper and easier just to purchase new system! However, Your last Post mentioned mixing of 100 and 133 Rams! Unl
Electronics Forum | Tue Jun 28 13:23:56 EDT 2005 | Bob Gilbert
Matt, Try a cooler profile by simply speeding up the conveyor by 10%. The difference may be the temperature the pads are reaching between the HASL boards and the Au boards. Are they the same thickness?
Electronics Forum | Fri Jul 01 11:03:11 EDT 2005 | smt_pro
We had this happen in a Heller 1808 oven when we placed Tant-A caps in glue (bottom side / no paste). We had our oven retrofitted to control the zone blower speeds. No more problem.
Electronics Forum | Wed Jul 06 10:22:04 EDT 2005 | PWH
At times we have had this problem with our AP25 due to one of the conveyor belts slipping. Load a PCB and check to see that both conveyor belts are running at the same speed. If not, tighten the one that is dragging. Hope this helps.
Electronics Forum | Thu Aug 25 19:53:48 EDT 2005 | Dave
If floor space is not too big a concern, don't forget about IPC9850 to really measure the true speed ratings of each PP machine.
Electronics Forum | Fri Jul 22 01:31:39 EDT 2005 | fastek
Peter- You're not going to solve this problem here. Call DEK.
Electronics Forum | Wed Aug 03 10:08:57 EDT 2005 | Me
Try this: http://www.adamtech.co.uk/support.html
Electronics Forum | Wed Aug 24 10:18:19 EDT 2005 | james
Well that Genius did it on this BGA. It does have a heatsink and absorbs alot of heat. It just stinks because the BGA cost over 1000 and I really can not scrap a board. But that first profile does not look correct for this board with the BGA esp.
Electronics Forum | Tue Sep 20 21:49:51 EDT 2005 | davef
2251 - Design Guide for the Packaging of High Speed Electronic Circuits 2252 - Design Guide for RF/Microwave Circuit Boards
Electronics Forum | Fri Oct 14 03:53:59 EDT 2005 | lupo
Hi, What is the speed of the conveyir (contact time) and alloy: Pb free or not? Temperature of bath? Quantity of flux? Regards