Electronics Forum | Tue Mar 22 07:39:05 EST 2005 | davef
There is no standard. This is a relative test. If you wish to do tests of this kind, we suggest to pay attention to the following points: * Shear strength of soft solder depends on the deformation speed applied. The faster the material is deformed t
Electronics Forum | Thu Dec 30 21:22:12 EST 1999 | Jim
Mike, Thanks for the reply. It's not really a matter of slope. It is the long term thermomechanical fatigue that the solder joint undergoes as a result of repeated severe temperature swings, while the product is in use. Non-leaded parts are suscep
Electronics Forum | Mon Aug 02 09:26:15 EDT 2004 | davef
Q1: How do you define torque setting for screw? A1: Talk to people at your nut supplier. Some nut suppliers post torque tables on the web. For instance: http://www.thelenchannel.com/1torque.html http://www.marfas.com/Ttorque.shtml http://www.pac
Electronics Forum | Fri Jan 21 14:51:08 EST 2000 | Dave F
Mike: I�d hate to see you making design decisions, based solely on the discussion here, but that this would be an impetus to consult IPC-D-279, "Design Guidelines ... " and take a course on designing reliable boards. Werner Engelmaier (Engelmaier
Electronics Forum | Fri Jan 15 16:55:50 EST 1999 | Chrys
| | | Hello, | | | | | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | | | | | So far, the tests I can think of performin
Electronics Forum | Thu Apr 20 22:46:26 EDT 2006 | samir
Amol, I thought I answered your question in another thread, dude! Anyway, to re-iterate. Yes, I was able to pull it off a hybrid profile. The LF BGA passed tensile testing, but no, it wasn't thermally cycled or stressed first to expose any latent
Electronics Forum | Fri Jan 15 17:13:07 EST 1999 | Earl Moon
| | | | Hello, | | | | | | | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | | | | | | | So far, the tests I can think of
Electronics Forum | Sat Nov 14 08:00:34 EST 1998 | Earl Moon
| Also the preheating of the board is done to help evaporate any water/alcohol that is in the flux - water is a big problem in No-clean processes. From our experience, a temp range around 200f - no more than 220f is ideal for the bigger boards, but t
Electronics Forum | Wed Jun 10 18:40:00 EDT 1998 | Earl Moon
| I am looking for the Industry standards on vias. Are they required to be plated with solder or is copper plating enough? What about reliabilty with either one? Also, if tenting the via is required should it be copper plated or solder plated over
Electronics Forum | Fri Jan 15 15:17:21 EST 1999 | Earl Moon
| | Hello, | | | | We are qualifying new sources of PWB vendors. We've got the first lot of "produciton" boards in and we want to put them through the paces before turing the vendors on. | | | | So far, the tests I can think of performing, and tha
winsouce.jpg)