Electronics Forum | Mon Aug 30 16:10:10 EDT 1999 | Dave F
| I have looked through the IPC web page and surfed to frustration. Can somebody give me a lead? | Brian: We don't use an etched board. We use a special stencil, described below and print on bare copper laminate. 3 Solder Wetting Test. Recogniz
Electronics Forum | Thu Aug 26 07:38:07 EDT 1999 | Robert Meston
Has anyone any experience in using Arlon thermabond as a prepreg between polyimide substrates and alluminium heatsinks, Does it really make any difference to the CTE etc ?
Electronics Forum | Sat Aug 28 14:23:52 EDT 1999 | JohnW
| Hi There, | | Could anyone please give me some pointers on screen printing non-conductive adhesives or where I could find the information avaliable. Aspects such as printing parameters, ideal stencil design and a general overview. Do already have
Electronics Forum | Wed Aug 25 14:40:24 EDT 1999 | hammer
Has anyone used bar solder from a company called "Electrum Inc." What kind of results did you have?
Electronics Forum | Tue Aug 24 11:29:59 EDT 1999 | Gary Kemp
Could use a little help here. Can anyone clarify to me the cause and fix of chip caps/resistors tombstoning following reflow? Any help would be appreciated. Thanks.
Electronics Forum | Wed Aug 25 09:53:40 EDT 1999 | lwk
| | | | Could use a little help here. Can anyone clarify to me the cause and fix of chip caps/resistors tombstoning following reflow? | | | | | | | | Any help would be appreciated. Thanks. | | | | | | | Most common reason is uneven heating where
Electronics Forum | Wed Aug 25 15:47:25 EDT 1999 | JohnW
| | | | | Could use a little help here. Can anyone clarify to me the cause and fix of chip caps/resistors tombstoning following reflow? | | | | | | | | | | Any help would be appreciated. Thanks. | | | | | | | | | Most common reason is uneven hea
Electronics Forum | Wed Aug 25 16:42:32 EDT 1999 | Dave
| | | | | | Could use a little help here. Can anyone clarify to me the cause and fix of chip caps/resistors tombstoning following reflow? | | | | | | | | | | | | Any help would be appreciated. Thanks. | | | | | | | | | | | Most common reason is
Electronics Forum | Wed Aug 25 21:44:03 EDT 1999 | Jason Tomlinson
| | | | | | Could use a little help here. Can anyone clarify to me the cause and fix of chip caps/resistors tombstoning following reflow? | | | | | | | | | | | | Any help would be appreciated. Thanks. | | | | | | | | | | | Most common reason is
Electronics Forum | Wed Aug 25 17:09:53 EDT 1999 | Earl Moon
| | Does anyone have any information on stencil aperture/pad ratios for noclean solder paste. In the past I have experienced severe solder ball problems when using the same size apertures from aqueous products as I do with the No-clean products. Co