Electronics Forum | Wed Oct 17 09:16:44 EDT 2012 | engineerjim
We are going through the motions of acquiring and setting up a new to us wave solder machine. My question, is any utilizing a solder/flux containment pan or other type system beneath the wave to help keep areas around the wave solder machine cleaner
Electronics Forum | Tue Nov 06 12:43:31 EST 2012 | deanm
4.2.7.1 states, ...If the bake temperature is not greater than 90 °C, there is no practical limit on bake time... If I interpret that correctly, then you may keep MSDs in a 40 deg. C oven indefinitely with no adverse conditions. Instead of opting
Electronics Forum | Sun Oct 28 01:55:12 EDT 2012 | dman97
Hi, Does anyone have a copy of the system software for a 265 Horizon? I need the base software version 06. I have the SP update CD's but they don't help. I am getting a base system software is missing so upgrade cannot be started message when I in
Electronics Forum | Thu Nov 01 12:58:40 EDT 2012 | bburn
My company is looking to purchase a new selective solder system. We're currently looking at the ACE KISS 205 and the ERSA Versaflow3. I am hoping to get some feedback from anyone who has worked with either of these machines or the companies themsel
Electronics Forum | Tue Jan 22 13:48:49 EST 2013 | smtequip
I would not consider KISS unless you have a limited budget and very low production volume as they are not well built enough to be considered "production" machines. That means they will not last as well as a machine from ERSA, Seho, or EBSO which coi
Electronics Forum | Sat Nov 03 11:08:24 EDT 2012 | anvil1021
We have experience with this alloy, but with enig and we did start with PB HASL, none of our PCBs would of course pass thermal cycling at normal temperatures with the HASL so we went to ENIG. we could thermal cycle at 100-115C with no issues. We foun
Electronics Forum | Sat Nov 03 11:20:35 EDT 2012 | davef
EricR: There's substantial information about the properties of solder alloys on the web. Here's an example of something that I clipped from one site Alloy ||Solidus (°C)||Liquidus (C°) ||Tensile Strength (psi / MPa) Sn42 Bi58||-E-||138||8000 / 55.2
Electronics Forum | Thu Nov 15 03:07:35 EST 2012 | nikyta
Thanks for your reply. As already said by Anvil1021, is not a good idea to mix Lead and Bismuth! Stay away from Bismuth if you have even the slightest traces of Lead on yours PCB, stencil, squeegee, spatula, blade, cleaning paper or cleaning cloths,
Electronics Forum | Fri Nov 02 14:22:20 EDT 2012 | marcelll
Hi, I'm looking for a copy of the Omniflo oven firmware. I'm talking about the model running under Win NT. Oven vintage is 1999-2001. Our oven is a 7 zones but I thing there's only one firmware for all the Omniflo ( 7, 10 12 zones . The original was
Electronics Forum | Wed Dec 12 02:26:35 EST 2012 | ryanmatthew
Hello Friends, Well Come to you. Simply, admirable what you have done here. It is pleasing to look you express from the heart and your clarity on this significant content can be easily looked. Remarkable post and will look forward to your future upd