Electronics Forum | Tue May 02 07:19:29 EDT 2006 | billyd
Good morning all. I'm trying to find some help on my voiding issue on my lead free BGAs. I am using a Heller 8/2 zone oven, and using Qualitek solder paste. I had listened to a tech representing another solder company, who told me to make the joints
Electronics Forum | Fri Oct 06 09:38:11 EDT 2006 | C.K. the Flip
Here's the BGA voids-reduction profile that I used: http://img323.imageshack.us/my.php?image=profileka0.jpg Keep in mind, this was for Sn/Pb BGA with Sn/Pb solder paste. For your situation, you might want to raise the peak temperatures to at least
Electronics Forum | Thu Oct 05 10:37:10 EDT 2006 | David
Hello all, We have problem with voids in one of our product. We are soldering IC (package SO8) with under the components grounding connection. The ground pad for this component has 3 via holes (before producing we have to cover this 3 holes from b
Electronics Forum | Tue Feb 12 17:57:42 EST 2008 | chef
I must ask the silly question- are you sure you deposited the correct amount of paste? Depending on aperature design-the voiding could come from a stencil that has its holes partially built up with old paste. If paste volume is guaranteed, then what
Electronics Forum | Mon May 25 08:37:28 EDT 2009 | d0min0
Hello, recently we changed supplier of the LF BGA, we did corossection and now have doubts... previous BGA specs : pitch 1mm, ball diameter 0.6mm future BGA specs : pitch 1mm, ball diameter 0.4mm on the crossecrion we found that one of the ball seem
Electronics Forum | Thu Jun 02 22:40:13 EDT 2016 | slouis2014
Hi, yes have a few experiments initially i tried to increase the solder volume but component pin have insufficient solder. 1. The solder coverage do you calculate it by solder volume or solder area. 2. if i would achieve as you recommend 50-60 % woul
Electronics Forum | Tue May 01 20:40:38 EDT 2018 | sarason
In the past I have worked on 600 Amp FET Blocks. The rule was no voids. The circuit board would be heavy copper. 4 times normal plating time. Not particularly high resolution on the board say 20 mils. To help with the heavy plating. The boards were t
Electronics Forum | Thu May 03 17:33:20 EDT 2018 | dleeper
Solder paste selection can have a huge impact on size and quantity of voids. Talk to a few suppliers and ask for their recommendation on low voiding formulas. Pick a few of your top candidates and then perform a DOE to see who has the best result. S
Electronics Forum | Fri Jul 27 09:47:20 EDT 2018 | davef
Adding to Rob's suggestions ... One of the theories about voiding in thermal / ground pads of BTC is: Solder starts melting at the edge of the pad and moves inward towards the center of the solder mass. This traps flux volatilizes. So, there needs t
Electronics Forum | Tue May 28 18:31:08 EDT 2019 | jlawson
Solder paste flux is main contributor, Lead termination chemical-oxide by products and PCB Plating-Chemicals. Reflow profile would have very limited if not no impact really unless is way off. Paste volume control and Stencil design plays a big part