Electronics Forum | Thu Jun 04 12:26:30 EDT 1998 | Dave F
| If you could measure and chart 3 variables in my process, what would they be? | The boards that I produce are on panels that are 12up and 2x4 up. All boards are single sided paper base w/o plated thru holes. They are on scored panels that measure
Electronics Forum | Mon May 24 16:18:16 EDT 2004 | Sue PH
I have been running this machine for seven years and is the only machine I have ever run. I used to joke with my supervisor that someday they should get a new machine, but only if I could take classes in Tahiti. Well, the old machine just purrs alo
Electronics Forum | Wed Nov 10 11:31:06 EST 1999 | John Thorup
Hello Horace You're lucky in that you have two of the same machine. You should be able to arrive at the root of the problem by comparison. The problem is likely to occur in one or more of these areas: MACHINE: As said , pump speed and air contact ar
Electronics Forum | Fri May 05 18:51:59 EDT 2000 | Steve Thomas
Looking for the best choice in books on soldering processes, primarily reflow but wave is going to be with us for a while so..... If you had to buy one today, which would you start with? Here's the list I gleened from the archives: Coombs, CF, "Pr
Electronics Forum | Fri Oct 09 15:06:22 EDT 1998 | Chrys
Dave F asked me for an update on the SRS we evaluated last month... I like this machine. Over 80% of your wave dross is actually good solder; you just can't get to it without some type of separating agent. I like the mechanical sepration method mu
Electronics Forum | Fri Oct 09 16:33:08 EDT 1998 | Dave F
| Dave F asked me for an update on the SRS we evaluated last month... | | I like this machine. Over 80% of your wave dross is actually good solder; you just can't get to it without some type of separating agent. I like the mechanical sepration met
Electronics Forum | Thu Dec 09 16:15:32 EST 2004 | Kevin
You should try looking into the Technical Devices Nu/Era. They offer the best warranty on their lead free solder pots. They use something called Titanium Nitride which has been tested to outlast Melanite. The dross produced on the TDC machines i
Electronics Forum | Wed Jun 21 09:22:29 EDT 2017 | emeto
Hello, I have an assembly that I am considering to run in a regular process(SMT, Wave)and afterwords solder 22 electrolytic capacitors. Due to the multi-layer board it is not an easy task, so I was wondering if you guys know any trick how to do that
Electronics Forum | Wed Jun 21 11:18:57 EDT 2017 | capse
Hello, > > I have an assembly that I am > considering to run in a regular process(SMT, > Wave)and afterwords solder 22 electrolytic > capacitors. Due to the multi-layer board it is > not an easy task, so I was wondering if you guys > know any t
Electronics Forum | Fri Jul 10 14:16:06 EDT 1998 | Bob Willis
As Steve said there should not be a problem with cracking plastic components but if you are reaching 180c there will be a problem with secondary reflow on the top side of the board. PCBs flex during wave soldering as they do during reflow if not supp
winsouce.jpg)