Electronics Forum | Fri Jul 13 10:57:04 EDT 2007 | dboudreau
Dear all, we are using the lead-free SN100C solder alloy for wave soldering. We are experiencing wetting problems each time we have to solder a thick board or a board with a large ground plane.I think that maybe we are not using the right flux. I w
Electronics Forum | Mon Feb 26 14:39:34 EST 2001 | John
We are developing a new product that will have hand placed through hole parts and double sided smt. This assembly will eventually be soldered to a plastic cover that has 15 insert molded terminals. The cover extends below the surface of the board,
Electronics Forum | Thu Apr 29 20:01:46 EDT 1999 | Jim W
| | I would like to know if there is any good training for Hand Soldering, Component Identification, Wave Soldering, and so on. | | | | I have seen two diffenent tapes and they were short and poorly done, I would like to buy some if I knew it had so
Electronics Forum | Mon Aug 17 19:43:43 EDT 1998 | Bill Schreiber
Smart Sonic has a new Model 2003 Stencil Cleaner that is designed to clean SMD adhesives, solder paste and post solder flux residue from wave solder pallets, oven air amplifiers, etc. all in the same system at the same time with the same chemistry. C
Electronics Forum | Fri Aug 12 14:11:20 EDT 2005 | pete_d
Bob, I've heard that many WSM manufacturers are not providing warranties for stainless steel solder pots that are holding SN100 because they are not completely confident that the SN100C alloy is non-destructive to the pot. fct�s own webpage states
Electronics Forum | Tue Sep 27 17:03:07 EDT 2005 | Jay Brower
Hi Steve, When I drain our wave solder pot in preparation for loading a lead free alloy (SN100); I am going to use muffin tins dusted with baby powder or maybe a little high temp oil so that the solder doesnt stick to the tins. I know that this may
Electronics Forum | Mon Mar 05 15:29:50 EST 2007 | ck_the_flip
When no-clean flux and no-clean soldering first came out in the late 80's / early 90's, there were lots of White Papers written about conformal coating adhesion and no-clean flux. I'm pretty sure all CC's will adhere to today's chemistries. To be o
Electronics Forum | Sun Oct 10 17:50:00 EDT 1999 | JohnW
| | We've recently encountered this problem where one of our .050" pitch BGA's were reflowing at the wave thus causing shorts... The board was profiled with probes stuck to a QFP solder joint, an 0603, and one of the BGA joints. There was an almost
Electronics Forum | Mon Aug 07 14:39:35 EDT 2000 | Claudine Corda
Kevin - Technical Devices Co. makes a table top wave station that should fit your needs. Their # is 310-618-8437. or try www.technicaldev.com. -Claudine cycorda@sono-tek.com
Electronics Forum | Fri Aug 12 03:38:32 EDT 2005 | md
Guys , Thanks for all your inputs on this one. I have had to increase preheats dramatically aswell as increasing conatct time over lambda wave. Joints are perfect. Cheers,