Electronics Forum | Mon Nov 02 22:57:02 EST 1998 | Kelly Gossman
Micheal, What does your profile look like for the wave? What profile does your flux say you need? My guess is it is not your profile, our testing with solder balls found that the mask on the boards was the largest contributor to solder balls. Wha
Electronics Forum | Tue Oct 06 15:41:14 EDT 1998 | Mike C
| | Does sombbody know what DPM rate a good and reliable SMT assembly line (incl. solder paste print, assembly and feflow soldering) has? | | DPM is Defects per million, usually measured on components. We run a process consisting of small to medium b
Electronics Forum | Wed Sep 30 18:43:46 EDT 1998 | Graham Naisbitt
Chrys, Please, refer firsatly to J-STD-001 Appendix D. Now, consider: SIR testing will help define the reliability of your finished assembly - it will not tell you how clean it is. Which do you or your customer prefer? Present SIR testing de
Electronics Forum | Tue Jul 28 02:28:48 EDT 1998 | Bob Willis
The causes for solder on gold are: Paste wash offs Dirty stencils Dirty under stencil cleaning cloths/no solvent Poor handling The most common reason is wash offs when there is a couple of balls left on the tabs and they reflow. With correct profile
Electronics Forum | Fri Jun 12 15:24:30 EDT 1998 | Steve A
| I am looking at purchaseing a full convection bench top oven from OK Industrys. (Model JEM-310) | It seems to have all the features that we will need for low volume production runs. | It has a Nitrogen input option, and I am intrested if anyone on
Electronics Forum | Fri May 29 17:48:34 EDT 1998 | Earl Moon
| | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not localize
Electronics Forum | Sat May 30 08:24:09 EDT 1998 | Dave F
| | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not locali
Electronics Forum | Sat May 30 12:51:29 EDT 1998 | Earl Moon
| | | | | We recently made the switch to no-clean and the wurface mount is turning out beautifully. However, the wave solder process continues to put up a fight; we are getting a white residue on the surface of the PCB. The residue is not loca
Electronics Forum | Tue May 26 19:20:39 EDT 1998 | Graham Naisbitt
Ryan, Please consider the following: There is no such thing as no residue flux. Low or no solids flux contain "wetting" agents to help the stuff stick upside down! Try painting your ceiling with less than 2% solids paint!! With all this excess liquid
Electronics Forum | Tue May 19 17:49:47 EDT 1998 | Earl Moon
| | | Earl, | | | I admit that I missed your article since I seemed to have let my subscription to Circuit Fabrication Magazine expire. I am interested in your experience in this area. Is there a way to get a copy of your paper? Could you maybe po