Electronics Forum | Thu Apr 11 20:35:22 EDT 2002 | davef
Messy. Messy. Messy. Consider gluing these components, until you control your process. It is unclear to us that a single factor drives these defects, but multiple factors that need to be tuned to work well together. PAD DIMENSIONS * Some SM-782 pa
Electronics Forum | Tue May 21 06:33:37 EDT 2002 | hayashi
*the other components are 0402 and SOIC 16, the > solderability were good. *the protection on the > terminations of microleadframe package is > Cu(copper),somebody call that leadless leadframe > package(LLP). *the time above 210 deg C is about
Electronics Forum | Wed Jun 26 08:54:53 EDT 2002 | davef
it has a lousy gage. * Solderability testing machines from different suppliers produce dissimilar results. * Tests don�t well represent in-use. For instance, how does one test the solderability of a BGA? [Ooo, ooo. I know the answer. => For BGA and
Electronics Forum | Thu Sep 19 21:23:42 EDT 2002 | davef
I'm not saying that an eraser will necessarily work. What I'm saying is that some erasers may cause more trouble than the eliminate. Look here http://aic.stanford.edu/jaic/articles/jaic28-02-003_2.html We prefer a brand called Ruby Red. The "ole
Electronics Forum | Fri Jul 11 10:00:05 EDT 2003 | davef
Component manufacturers recommend limits on the power and period of ultrasonic cleaning. Examples are: * PRECAUTIONS AND GUIDELINES MULTILAYER CERAMIC CAPACITORS: (9) Ultrasonic cleaning time shall be ten minutes maximum. When the power of ultrasoni
Electronics Forum | Wed Dec 17 03:26:17 EST 2003 | Kev
Hi Lads, Thanks for all of the replies. To answer a few of your questions..... My wave is a Hollis PT500N. It has 3 zones of pre-heater rod elements. Each individual element (601195-01) is 500 watts. There are 16 elements per zone so 8 Kw per zone.
Electronics Forum | Fri Feb 20 13:01:26 EST 2004 | Jay
First, it depends on the alloy composition of the solder. As you might know, eutectic Sn/Pb solder has the lowest melting point among available conventional solder systems. (except those based on Sn-In and Sn-Bi systems.) For example, 63Sn/37Pb - 183
Electronics Forum | Thu Mar 04 19:27:33 EST 2004 | russ
what I have usually found although not from wave conveyor chains but from racing motorcycles is that binding is caused by wear and bending and not dirt unless it is excessive to the point that you can actually see the dirt that is binding it. When t
Electronics Forum | Thu Mar 18 09:25:27 EST 2004 | remullis
Normally when I run into having to hit the ESC key to step through this is the steps I take. 1. Power machine down and restart. 2. Home machine and watch cutter carefully. Both cutter should acuate and the height motors should run CW and CCW. 3. You
Electronics Forum | Wed Apr 07 22:15:31 EDT 2004 | davef
We're not familiar with the AUG5 from Taiyo. [It doesn't show on their US site.] Is it liquid photoimageable? Printed solder masks are more likely to bleed. But you wouldn't have any solderability with bleed. Your plating seems acceptable [if th