Electronics Forum | Fri Mar 24 17:07:39 EST 2000 | John Thorup
Hello Ashok If you are talking about the thousands of volts that is often generated by either simply unrolling the tape to apply or when it is removed from the board after soldering you don't have a lot of choice since it is an insulator. Ionization
Electronics Forum | Mon May 07 16:49:59 EDT 2001 | davef
Ashok, What in earthly heaven does this question have to do with "site support"? You can�t always get what you want, but sometimes you get what you need. Some leads are: * The proposed IPC cable/wire harness document is now IPC/WHMA-A-620 and go
Electronics Forum | Thu Jan 27 20:34:12 EST 2000 | Dave F
Ashok: The real concern about moisture sensitivity is in plastic packaged parts. The plastic packaging used to manufacture surface mount technology devices absorb moisture from the environment. The high temperatures involved in vapor phase/reflow
Electronics Forum | Tue Aug 24 15:30:51 EDT 1999 | John Thorup
| | This is out of the normal scope of this site but� | | | | I am in search of a Digital Camera for use with documentation instructions. What would be the Minimum Resolution that I should require? I will need details of assemblies such as Compone
Electronics Forum | Thu Aug 19 13:43:59 EDT 1999 | Earl Moon
| | OK folks, let's get real serious. | | | | Well, I shot off my big mouth yesterday during a scheduling meeting concerning DFM and rework. Again, what an irony, oxymoron, or that other thing. | | | | Anyway, I said it would take another 4 weeks t
Electronics Forum | Thu Aug 12 09:02:08 EDT 1999 | Gian.D
| Hello, | | Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | |Good! could you suggest some suppliers name or address or web site or e.mail...
Electronics Forum | Sun Jun 20 06:30:49 EDT 1999 | Scott Cook
| Do anyone have any experience on assembling high frequency product, 1.8GHz or 2.4GHz. | | In our production line, we manufacture 1.8GHz product with using no clean paste (RMA type) for reflow and no clean wire for rework. In our functinal test,eit
Electronics Forum | Sun Jun 13 05:46:21 EDT 1999 | Brian Ellis
Murray "No-clean" fluxes/pastes should not normally give "white residues". Before exploring cleaning, which is costly for small production levels, I suggest you may care to find out why you have these residues. To help you, can you please answer th
Electronics Forum | Tue Jun 08 12:49:41 EDT 1999 | Dave F
| Hi,my master | How to iron out such soldering bridge with below conditions: | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | 3.using spraying fluxer and n
Electronics Forum | Tue Jun 08 13:06:53 EDT 1999 | Kevin Hussey
| | Hi,my master | | How to iron out such soldering bridge with below conditions: | | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | | 3.using spraying fl