Electronics Forum | Fri Jul 16 13:49:31 EDT 1999 | Timothy O'Neill
| | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | What is it you're trying to do? | Dealing w
Electronics Forum | Sat Jul 17 03:02:58 EDT 1999 | Jeff Sanchez
| | | | | I need a good chemical to remove the lacquer finish off of magnet wire. I know there are different kinds but I need one that really works. Any suggestions would be great. thanks in advance guys. | | | | | | | | | What is it you're trying t
Electronics Forum | Thu Sep 10 09:44:05 EDT 1998 | Earl Moon
| | Can anybody point me to a Standard that provides details on the use of Wire Links for the repair of SMT PCBs, e.g. the maximum number of permissible links, the material to be used, the method of joint etc.? | Dave: ANSI/IPC-R-700 answers many of
Electronics Forum | Thu Sep 10 17:26:56 EDT 1998 | Dave F
| | | Can anybody point me to a Standard that provides details on the use of Wire Links for the repair of SMT PCBs, e.g. the maximum number of permissible links, the material to be used, the method of joint etc.? | | Dave: ANSI/IPC-R-700 answers man
Electronics Forum | Tue May 28 17:50:20 EDT 2002 | myu
Hi, Everybody! I'm looking for a High-Temperature Solder Paste / wire: "Pb93WROL140.71454";or "00Z890"; J-STD-006 Solder Alloys Sn05Pb93Ag02B Sn% Pb% Ag% Solid C Liq C Solid F Liq F 5.0 92.5 2.5 280 284 536 543 It should meet IPC/J-ST
Electronics Forum | Thu May 30 10:45:16 EDT 2002 | sjpence
We got a similar alloy Sn05Pb93.5Ag1.5, of Alpha Vaculoy bars. It is not the eutectic alloy you were looking for but it is close. This alloy and similar high temperature alloys are used in downhole electronics and so a supplier in the Houston area
Electronics Forum | Thu Jan 02 21:54:18 EST 2003 | jonfox
This should be a fun one! I was asked the question from our Engineering, should we use die attach with wire bond or go ahead into the new world of flip chips? Right now, I am faced with information overload about the two processes but I am really l
Electronics Forum | Fri Mar 21 20:21:41 EST 2003 | Grant
Hi, I can verify that, and we have done 2 or more reflows with prototypes, using vapor phase reflow, and because there is no oxygen, the result is good, and you cannot tell the difference between the first reflow, and the 3rd. We are getting a vap
Electronics Forum | Mon May 12 10:48:49 EDT 2003 | Theresa Woodford
Does anyone have any experience with plasma cleaning? I currently have an IMS Substrate (10-15 microinch gold flash over electroless Ni) attched to Ryton PPS / R40 walls (40% glass filled/compression molded). The wall is being attached to the IMS u
Electronics Forum | Thu Sep 04 19:20:39 EDT 2003 | severs
Fine magnet wire responds well to abrasion stripping. Here's one I've used: http://www.carpentermfg.com/magnet.htm Teflon requires a different kind of stripper called a twin blade rotary stripper or a precision die stripper because it's subject to
winsouce.jpg)