Effects of Reflow Profile and Thermal Conditioning on Intermetallic Compound Thickness for SnAgCu Soldered Joints
Published: |
April 29, 2010 |
Author: |
Jianbiao Pan, Tzu-Chien Chou, Jasbir Bath, Dennis Willie, Brian J. Toleno |
Abstract: |
The purpose of this paper is to investigate the effects of reflow time, reflow peak temperature, thermal shock and thermal aging on the intermetallic compound (IMC) thickness for Sn3.0Ag0.5Cu (SAC305) soldered joints.... |
You must be a registered user to talk back to us. |
Company Information:
More articles from Flex (Flextronics International) »
- Jan 23, 2019 - AOI Capabilities Study with 03015 Component
- Jun 15, 2017 - Nondestructive Inspection of Underfill Layers Stacked up in Ceramics-Organics-Ceramics Packages with Scanning Acoustic Tomography (SAT)
- Oct 27, 2016 - Press Fit Technology Roadmap and Control Parameters for a High Performance Process
- Sep 01, 2016 - Reliability Study of Low Silver Alloy Solder Pastes
- Aug 18, 2016 - Selective Reflow Rework Process
- See all SMT / PCB technical articles from Flex (Flextronics International) »
More SMT / PCB assembly technical articles »
- Mar 19, 2024 - What is Underfill | GPD Global
- Mar 19, 2024 - Made in Japan: Solder Paste Jet Dispensing Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 26, 2024 - Precision Control in Electronic Assembly: Selective Wave Soldering Machine | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Feb 02, 2024 - Maximizing Efficiency: The High-Speed SMT Line With Laser Depanelizer | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Dec 27, 2023 - Revolutionizing Tech: SMT Auto IC Programming Machine Mastery | I.C.T ( Dongguan ICT Technology Co., Ltd. )
- Browse Technical Library »
Effects of Reflow Profile and Thermal Conditioning on Intermetallic Compound Thickness for SnAgCu Soldered Joints article has been viewed 1000 times