Mantis: Kenny reflows paste on [wave solders] all via, not just the test via, to plug the via and provide for a pressure seal between the board and the test fixture. Beyond that, since solder is softer than copper [and fills the hole better], solde
Electronics Forum | Mon Jan 15 15:40:18 EST 2007 | pyro747
Having problem with a 2X50 SCKT Strip PTH component(fine pitch) bridging on the wave. The PCB runs in wave pallets. Just wanting to know what successful findings have been done to eliminate bridging? Pallet angles? Copper or titanium inserts? Air kni
Electronics Forum | Mon Sep 17 05:48:10 EDT 2012 | stivais
Hi Ben, Yes, this could be the reason but have you ever seen solderability issues for (new) boards with LF-HAL surface finish? I have seen this only if there are surface finish quality issues for bare boards (exposed copper etc.). In this case we di
Electronics Forum | Fri Oct 01 00:44:41 EDT 1999 | Hon Choi
If permanent set processing is used, designate the permanent set table name (PST). The Separator uses the PST to restrict the allocation of specified parts to certain feeder positions on the unit (device) table. The PST is mainly used for efficiency
Electronics Forum | Wed Mar 14 09:07:34 EST 2001 | blnorman
We just ran a study to try to determine this. We exposed the paste to 85% humidity to simulate worst case manufacturing. At various times we removed the paste from the chamber and tested it for tack, solder balling, wetting (copper coupon), and vis
Electronics Forum | Tue Dec 01 09:02:18 EST 1998 | Earl Moon
| | | Hi folks , | | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most. Our in
Electronics Forum | Fri Dec 04 20:26:34 EST 1998 | kallol Chakraborty
| | | | Hi folks , | | | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most. Ou
Electronics Forum | Fri Dec 04 20:37:45 EST 1998 | kallol chakraborty
| | | | | Hi folks , | | | | | Lately we are seeing a lot of rawcards with black spots on the pads - most of them have Au finish(immersion gold) . We did a lot of inspecton after wave solder and found that only (fine pitch) QFP are affected the most
Electronics Forum | Wed Jun 26 08:53:32 EDT 2002 | davef
We have not done a DOE on board warping. Consider: * How close the board gets to its Tg during the reflow cycle * Amount of copper on each side and the balance between the two * Thickness of the board * Overall length x width * Time at temperature
Electronics Forum | Mon Jan 24 06:19:04 EST 2011 | fönsi
Hello! I've had the same problem about one Jear ago. We had exessive building of voids in the solder joints. I recomment to take a pincer to break off some of the components. If the solder joint is good, the copper pad will stay at the solder joint