Electronics Forum | Thu Apr 05 09:18:14 EDT 2007 | pjc
Please note that pin holes and blow holes are not always defects. The latest IPC 610A Rev D workmanship standard has them as process indicators- depending on Class. I don't have the document handly while writing this. It would be good to look that up
Electronics Forum | Wed May 09 13:37:07 EDT 2007 | jmills
Greetings Tried to search past threads without an answer. I have a resistor that just fits the between pads. Some of the resisitor were installed without the termnation sitting on the pad and are infact sitting on solder a good .020 to .025 above th
Electronics Forum | Fri Feb 17 13:10:34 EST 2006 | amol_kane
I have Immersion Ag and Immersion Sn LF boards that were waved using SAC305 alloy. I have a lot of tears/shrink voids in the waved connections. I am aware that SAC305 in wave has a propensity of shrink tears/voids due to the non eutectic property of
Electronics Forum | Thu May 11 12:44:04 EDT 2006 | slthomas
One of our customers' products has a couple of adjacent 0603 packages (one resistor, one cap) that are .010" apart. They are side by side, not end to end. The adjacent pads between the two parts are electrically connected so bridging isn't an issu
Electronics Forum | Thu Feb 10 11:40:25 EST 2005 | Carol
Hello All, Can somebody direct me to a facility or school or even a business that can offer an x-ray course for Class 3 electronic circuit board population interpretation, as in BGA ball acceptance, connector solderability fill acceptance etc.? Some
Electronics Forum | Wed Feb 28 00:01:47 EST 2007 | Muhammad Haris
Hi, The distance between the two terminations/endings/pads of 0603 (0201)is 0.15mm i.e. lesser than than the distance between the 0603 and through hole i.e. 0.5mm My ques is that, then why its termination doesnot short as it has a minimum distance.A
Electronics Forum | Thu Aug 07 22:51:05 EDT 2008 | davef
We expect aerospace to be IPC-A-610, Class 3 and J-STD-001, Class 3. The above quality statement stecifies: * "IPC 610, Class 2 acceptability." This is unclear. Should this be "IPC-A-610, Class 2 acceptability?" * No class for J-STD-001. Should we a
Electronics Forum | Tue May 26 14:39:40 EDT 2009 | boloxis
QFN or MLFs are mainstream now, QFNs already evloved to much more complex versions now like matrix pins, stacked dice and flipchip versions. IPC 610D already includes them, just make sure the pins have solder plating, the PWB pads have soldermask in
Electronics Forum | Wed Jun 17 16:02:09 EDT 2009 | mhunter
Any thoughts on this will be appreciated, thanks in advance for reviewing. This assembly has been processed in our facility by going through a press operation (~ 1731 lbs), then into wave solder. Note the discoloration around the pemnut. The discol
Electronics Forum | Mon Jan 12 21:31:26 EST 2015 | warwolf
The closer your inspection the more defects you will find, the more rework you do the possible cost you will add and the potential increase of damage you could do to your products if rework is not up to a machine copyable standard. "Is there any in