Hi all, Does anybody have any comments on the lead-free alloy SN100C from AIM solder? I am in the process of selecting the "right alloy" for our lead-free wave solder machine. We manufacture A/V equipment. I appreciate your feedback as usual. Hir
Electronics Forum | Fri Sep 02 06:47:17 EDT 2005 | dougs
Is there a standard that we should aim for in respect to the strenght of the solder on SMT leads? We have a customer who are testing our product by pulling leads off of pads then returning them.
Electronics Forum | Wed Apr 14 13:39:48 EDT 2004 | procon
Also check out AIM's NC368 / LF218 www.aimsolder.com
Electronics Forum | Fri May 05 09:00:46 EDT 2006 | russ
Studies showed that there are no issues mixing SN100C and SAC305, I believe that AIM has this info. Russ
Electronics Forum | Fri Jul 08 10:13:15 EDT 2005 | fctassembly
Hi Jason, Did the SAC paste wet other board finishes adequately? I have seen no issues to date with solderability of SN100CL HASL boards with our No Clean pastes. Regards, Bob
Electronics Forum | Fri Jul 08 09:14:49 EDT 2005 | Jason Fullerton
I've tested boards with SN100C HAL finish, and wetting to the PCB finish was poor at best, using a no clean SAC305 paste.
Electronics Forum | Wed Jul 27 09:47:01 EDT 2005 | GCampbell
CEMCO Uk have done testing using SACX0307, SAC305 and Sn/Cu/Ni. The copper dissolution tests (report available) conducted at CEMCO showed that the lowest copper erosion rate was achieved by SACX0307. Regards Gerry
Electronics Forum | Wed Jul 27 16:39:18 EDT 2005 | GS
Hi Gerry, do you think it is possile to get copy of the report? Thanks and Regards GS
Electronics Forum | Wed Jul 27 17:18:07 EDT 2005 | Carl
Any issues in your experience using SAC305 for reflow and SN100C for wave on ENIG pcbs? I've seen the CD, but there's not much specific data regarding ENIG pcbs Thanks