Electronics Forum | Tue Mar 12 10:16:05 EDT 2013 | bocci572
Yes the components are flat and no larger than 50mm in size. Most are full rings or just an arc of a ring. I understand fully the best way to have the capabilities proven would be to have the vendor demonstrate. I am kind of looking at what people
Electronics Forum | Sun Mar 24 17:28:20 EDT 2013 | vikkaraja
Thanks for all the help you are giving me but I just can't put my finger on this annoying problem. I checked and recheck all sensors without much sucess against the I/O. Something I am not understand is these two followning conditions--- first one I
Electronics Forum | Fri Apr 05 07:17:55 EDT 2013 | leemeyer
I've never seen one but i've been told that there is a 2 tier vib plate where the top plate is set back a bit so that the nozzle can pick from the top and bottom plate. OK so you have the plates on the machine and have entered their coordinates. Cl
Electronics Forum | Fri Apr 05 18:22:18 EDT 2013 | Adam
We have two ZipaTec 460s Selective Solder Machines, one for Lead and one for Lead-Free. This morning we noticed the solder pot was covered in solder balls, and after asking the operator what they had run, the answer was "Nothing." The operator had al
Electronics Forum | Thu Apr 11 11:24:55 EDT 2013 | markhoch
Thank you for your advice Eric. Different SMT Machine Platforms have different methods for handling these PCB Panels with bad circuits. (Commonly known as "X-outs"). Some platforms allow you to identify X-Outs simply by darkening in the first fid
Electronics Forum | Tue Apr 23 15:18:02 EDT 2013 | davef
2 oz copper should be 2 oz per ft^2 thick. There is no relationship between thickness and copper weight due to the effect of processing. Since this is a painful way of thinking about things, ppl have reached a compromise and talk about 'nominal thick
Electronics Forum | Mon Apr 29 12:32:18 EDT 2013 | stephendo
Do you watch when it is doing the wave height test? Watch it and see if it goes up to the same spot on the test probe each time. If the test probe is dirty sometimes the solder has to go up higher on it before it gets detected. You might actually be
Electronics Forum | Mon Apr 29 13:56:19 EDT 2013 | williamaxler
We have a Versaflow 40/50 and ours is setup like this. We have out nozzle test position set so that in the Z axis you are 3.8mm away from the pin. Used feeler gauge Then you can set your gradient per nozzle. Start with a number then do a wave offs
Electronics Forum | Tue Apr 30 05:05:16 EDT 2013 | pavel_murtishev
Colleagues, Now I am involved into plant ramp-up where 3x Panaconic NPM-W will be installed. New production hall is being designed right now and the problem is that constructors have never met SMT shops and know very few or next to nothing about requ
Electronics Forum | Thu May 02 15:29:19 EDT 2013 | jim_n_hky
I can't answer your specific question on the floor, but I have some suggestions. The equipment manufacturer should be able to provide the floor loading requirements. A structural engineer should be able to translate that into specs for hte constructi