Electronics Forum | Tue Jun 13 08:17:06 EDT 2006 | davef
The solder alloy does not change based on the flux. Your potential for embrittlement is the same [providing the metal of the solders are the same] with either solder. We would guess the OA flux is [and drag tinning are] removing corrosion from the
Electronics Forum | Mon May 06 12:20:09 EDT 2013 | davef
Gold in solder alloys can be brittle. We always used to talk about keeping gold LT 3% in order to avoid embrittlement. Some military contracts require removal of gold from soldered contacts. Adding gold to a solder alloy that you're familiar with wi
Electronics Forum | Thu May 02 09:33:30 EDT 2013 | 15009
Looking for advice on soldering lead free paste to a board with very heavy gold plating. I have learned from the Customer that this is HARD GOLD and that it is 10-20 Micro Inches Hard Gold over 100 Micro inches of Nickel. When we reflowed the solde
Electronics Forum | Fri May 24 09:16:36 EDT 2013 | grahamcooper22
you need to reduce your time above liquidus to as low as you can...maybe 10~30 secs to allow the solder to wet to the gold but minimise the amount of gold that is dissolved into the solder joint...try also reducing the peak temp to 200~210 deg C. Thi
Electronics Forum | Fri May 03 16:06:44 EDT 2013 | hegemon
To be short, no change in profile is going to get you through this. As I recall the point of hard gold is to retard the wetting process, so no surprise here. For example a connector might have hard gold plating at the mating surface, but not at t
Electronics Forum | Fri Dec 03 19:44:34 EST 1999 | Russ
Hello all, I am in the process of converting our facility to noclean processes. So far I am experiencing troubles with soldering to gold finishes. The finish is an H.P. type1. The solder joints appear dull and grainy. They seem to be very strong
Electronics Forum | Mon May 20 15:43:01 EDT 2013 | ngotranbestek
Hi I meet problem by PCB with diameter 300cm and thick 6mm i used tin-lead with profile normal, soak time 60-90 sec, Temp peak is 220 degree C, But solder see not good, not shiny. Any body recomend help me to fix this problem for Hard gold playing.
Electronics Forum | Mon Jun 12 07:42:56 EDT 2006 | brian.perry@suntroncorp.com
We are placing a gold plated device (LCC) to a NiAu PCB using a SnPb No-clean solder. We're noticing quite a bit of difficulty with reliable joints (intermittent connectivity) and if we have to rework a particular device, adjacent devices of this sa
Electronics Forum | Fri Apr 13 21:02:19 EDT 2007 | Sam
Anyone experience using SnPb wire to gold plated ICs? I have tried to solder the SnPb wire to the gold plated ICs lead, but the surface finishing is dull. Can anyone explain that to me? Why it is not shinny surface? Any recommendation?
Electronics Forum | Sat Apr 14 09:28:58 EDT 2007 | davef
When soldering a component to a board, the solderability protection on the component combines with the solderability protection on the board and the solder to form an alloy. This alloy is unique for that combination of solder and solderability protec