Electronics Forum | Tue Sep 23 15:27:17 EDT 2008 | slthomas
You'd still have to change all of the part library references, make up new ones for new parts, enter feeder sizes, etc. More trouble than it's worth, once you know how to use the software and prep your cad data to be compatible with it. There are lo
Electronics Forum | Tue Oct 07 03:03:06 EDT 2008 | rafacadiz
We had the same problem last year. You need verify these key points. 1- Holes are drill, NOT PUNCH. 2- Inspect 100 Boards at microscope, and verify that there is not rest of fibers in the holes. 3- Meassure the dimensions of the holes. a) virgi
Electronics Forum | Tue Apr 07 15:36:15 EDT 2009 | gtemkin
Most of the conformal coating manufacturers recommend verifying the compatibility of their coating with the solder mask, so it's no surprise that occassionally there will be such issues. Are you sure your conformal coat is completely cured? If your
Electronics Forum | Fri May 29 03:27:36 EDT 2009 | grantp
Hi, I have only handled MYDATA and Fuji personally. MYDATA was not realiable, Fuji's are perfect. As for feeders the XP series, we have 5 of them, and they all use the same feeders as the older machines such as CP and IP series. The XP can even use
Electronics Forum | Fri Jun 25 12:19:52 EDT 2010 | operator
I have always been under the impression that you want the flux make-up of your cored wire and supplemental flux (squeeze bottle) to be as identical/compatible as possible. I was just looking over a manufacturers datasheet for a resin-based cored wir
Electronics Forum | Thu Sep 16 09:29:21 EDT 2010 | san_1023
Weller and Hakko have some good soldering > stations, hot air SMD rework system and BGA > rework systems: _a class=roll > href="http://www.wellersoldering.blogspot.com/" > target="_blank"_http://www.wellersoldering.blogspo > t.com/ _/a_ I am t
Electronics Forum | Mon Jan 10 16:58:48 EST 2011 | piter
Hi Ripal it seems that you have problem with compatibility of alloy and quality of solder balls. First check solder alloy form BGA balls what is it?(SAC105,SAC305, etc.) what type of solder paste you use?? third thing is what type of finishing you h
Electronics Forum | Tue Aug 23 18:14:06 EDT 2011 | jlawson
vapor degreaseing has two main flavors mono solvent and co-solvent. the later being the best performance Yes can clean PCB and in many ways is best in cycle time and cleaning quality. Is batch machine based usually or automated batch if budgets all
Electronics Forum | Tue Nov 08 21:56:23 EST 2011 | tpappano
Hi Jeff, both units have DC servos, and both appear to have the same vision system, although #2 has an additional upward-looking camera with a high magnification lens for die mounting. If I could make use of your hex files, that would be great sinc
Electronics Forum | Thu May 10 14:43:47 EDT 2012 | davef
fluxer => cleaning (or lack there of) => conformal coating: there is a lack of compatibility. You need to figure-out which is the bad boy. Maybe a good guess is to conformal coat boards at each step in the process and then have them tested. Don't de