Electronics Forum | Wed Oct 20 01:43:34 EDT 1999 | Jorge L. Torres
We have a Yamazen PK-32E Magazine board Loader. It appears that at one time or another was connected with a Sanyo Pick & Place machine, which is a 24VDC system for SMEMA. I want to connect it to the DEK265 printer, which currently has an inspection s
Electronics Forum | Thu Nov 21 01:01:33 EST 2002 | chao liang
Who had building the f4g and c/c server , when I set up the f4g and the c/c server I found them could not transportion , The FTP could work in normal ,the error code is 417c0021 :c/c connection to failed ,[cann't connect local socket [ connect :10060
Electronics Forum | Thu Nov 21 01:02:06 EST 2002 | chao liang
Who had building the f4g and c/c server , when I set up the f4g and the c/c server I found them could not transportion , The FTP could work in normal ,the error code is 417c0021 :c/c connection to failed ,[cann't connect local socket [ connect :10060
Electronics Forum | Wed Mar 02 09:19:15 EST 2005 | Dilbert
You probably are aware of this, but somehow get the conditioning unit as close to the sensor as you can. It sounds like the problem is the "long twisted pair shielded cable". Try different means of shielding, connect the shield at the end that has
Electronics Forum | Tue May 16 14:05:44 EDT 2006 | Mike
Hello, Heres my take. If the ends that are touching are connected by trace, and IPC-610 is satisfied, and the connection does not make a Parallel circuit where a series circuit is required, then I would treat it as a process indicator. That is, unle
Electronics Forum | Thu Aug 20 21:52:22 EDT 2009 | davef
It's a safe bet that your solder alloys will merge and form a proper solder connection at ~230*C for 15 to 20 seconds. At process conditions with less time and temperature, it's a lot of bla-bla-bla. In order to understand the quality of the solder c
Electronics Forum | Wed Mar 23 11:08:36 EDT 2011 | davef
There is no such standard, nor should there be. The important thing is to make good solder connections. That's IPC standardization focus, defining good results of manufacturing process. The approach that you take in developing the process of making g
Electronics Forum | Fri Jul 15 12:15:08 EDT 2022 | aj3
Does anyone have any documentation or knowledge about the S3088-III or 3088 Basic Viscom AOI machines? I am trying to determine if I can pass the data it outputs to a 3rd party vendor, and I need to know the connection method (local network, internet
Electronics Forum | Mon Nov 17 21:30:10 EST 2003 | davef
Odds are that all of the completed product had corroded leads, if the components came from the same load / were processed similarly. ... but the issue is NOT corroded leads. The issue is well soldered connections. * If the solder connections on the
Electronics Forum | Sun Apr 24 09:12:00 EDT 2005 | davef
We're not sure what your customer is talking about either. Gold and tin form an intermetallic compound [IMC] that can cause poor solder connections. To minimize the potential of a problem, keep gold to less than 3 percent of the metal. [Search the