Electronics Forum | Sat Apr 14 00:04:21 EDT 2001 | zam_bri
I'm not a Wave soldering guy and my friend have asked me a question on what is the best preheat time and temperature for Wave soldering.They experiences only 10% flow up thru the PTH barrel. I've asked them to increase the temperatue to 120 Deg C. Cu
Electronics Forum | Sun Oct 31 08:27:09 EST 1999 | Dave F
David: I think it's great that you are getting that much barrel fill with STEEL leaded components!!! So, what kind of steel are the leads are made from? How much corrosion is on the leads? Frankly, I don't believe that the leads are made of steel
Electronics Forum | Tue Nov 02 23:34:58 EST 1999 | chartrain
You appear to have two problems working against you at once. One is component lead corrosion that the no clean flux isn't aggressive enough to remove. Do a simple dip and look test. Flux the leads of a component and dip it into the molten solder for
Electronics Forum | Tue Nov 02 17:52:17 EST 1999 | Dave F
Jim: Several points: 1 If you�re correct about corrosion of your component leads (which is entirely possible if the leads are steel, as you say), then the AIM 264-5 no-clean may not be aggressive enough to remove the corrosion you are seeing routin
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Fri Nov 05 21:41:46 EST 1999 | chartrain
Temperature vs time is what soldering is all about. The faster you run your conveyor, the more heat will have to come from the pot for a given assembly. Example: You heat the board to 200F top side through the preheaters. Eutectic 63/37 melts at 361.
Electronics Forum | Wed Jun 12 04:02:00 EDT 2019 | liyunqiong
SMT reflow soldering temperature setting and process flow: The influence of SMT reflow process parameters on the key parameters of reflow soldering temperature curve provides reference for the setting and adjustment of reflow soldering process para
Electronics Forum | Tue Sep 25 14:08:59 EDT 2001 | davef
Oooo, the solder on the pad and PGA ball is flowing during reflow down the via to the secondary side? Why didn�t you say so?? ;-) Why would you expect that gravity and capillary action wouldn�t force solder to flow down the solder plated via to the
Electronics Forum | Fri Feb 03 07:06:22 EST 2017 | emeto
It makes sense. With temperature viscosity will change, and more liquidus material will flow better.
Electronics Forum | Tue Dec 16 09:01:52 EST 2003 | tds
What model is your Hollis? Does it have the coil heater?