Electronics Forum | Thu Jan 06 04:20:50 EST 2000 | R Lahat
Vishy, I was in the same boat. I had to run 3 siemens smt lines and get good results. I used the Arena simulation software to program in my 3 smt lines and found it very complicated but can be done. In parallel I took in industrial engineering stude
Electronics Forum | Mon Dec 20 17:30:30 EST 1999 | g cronin
bill is right about finding a reputable dealer, i do have a horror story about buying a machine that was not what it was sold to be. But there are some good ones out there.. if you do have interest in a machine feel free to ask the forum our opinion
Electronics Forum | Thu Oct 28 15:28:07 EDT 1999 | Bill Haynes
Hany, ESD mats, in my opinion, are very important. Why jepordize the quality of your product. We use sheets of stainless steel around all areas that are ESD sensitive and ground them to the machines. Of course they are no good unless the people st
Electronics Forum | Thu Aug 05 08:04:32 EDT 1999 | Peter Barton
| Hi , | | Could DIP package ( PTH) run through IR Reflow instead of wave soldering? | | Will there be any reliability impact on this package. | | Thanks | | Jack | | Jack, The dip component package material and the packaging process is the sa
Electronics Forum | Wed May 26 11:12:43 EDT 1999 | Scott S. Snider
If you truly want a GOOD Career I believe you must get out electronics manufacturing and find something that is more fulfulling. Try something that allows for family time. | Hello everbody! | | I was wondering if any of you have any GOOD recomen
Electronics Forum | Mon Feb 15 15:43:06 EST 1999 | Dave Jurena
Hope some of you out there can help me with this one. I am getting feedback from our test department that they are showing opens on solder joints which have visually good wetting. The touch-up operators confirm that the joint looks good. All they do
Electronics Forum | Mon Jul 06 08:36:26 EDT 1998 | Steve Schrader
| What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good joi
Electronics Forum | Mon Jul 06 12:05:56 EDT 1998 | Srirama T. Reddy
| | What should a good gold joint look like? We've run boards for our customers that look kinda dull but seemed to wet properly and the boards fired up just nicely! Should they look nice and shiny like our HASL boards or is "a shiny joint is a good j
Electronics Forum | Mon Apr 06 10:32:53 EDT 1998 | Justin Medernach
| Peter, | Take a look at IPC-ANSI J-STD-001A and B, J-STD-004 and I think, 005/006 which cover solder paste (?) I think. | Whatever, they do reference one another. | | Question: Whatparameters are used to determine "good" Solder Paste? What refer
Electronics Forum | Sat Jan 24 16:05:06 EST 1998 | Bill
| We are an embedded computer company that does our own assembly. | We currently use a "home grown" software creation to track our | product quality. I am interested in replacing this software | with an "off the shelf" solution, if possible. Do y