I've been involved with no-clean flux and conformal coat in the past.It has been my experience that the amount of no-clean flux used is proportionate to how well the conformal coat adheres to the boards.No clean paste did not affect adhesion. The co
Electronics Forum | Mon Sep 12 14:08:33 EDT 2005 | Amol
The fluxes used in the board manufacture are RMA fluxes. The board is cleaned according to the IPC standards and tested to ensure quality. I am thinking of designing a DOE to isolate the problem
Electronics Forum | Sat Jan 06 22:09:53 EST 2001 | Greenman
Cory, I've got a lot of experience of testing of this type. The physical (not chemical) nature of the flux residues is the crucial issue in compatibility. If you have a softer residue (either caused by a thick initial solder paste deposit, or a low p
Electronics Forum | Thu Jan 16 15:16:52 EST 2003 | Mike Konrad
You are comparing apples to oranges. No-clean fluxes, because they are designed not to be cleaned off after reflow, contain very low solids. Normally, no-cleans have a solids content of 2% - 5%. Your basic RMA has a solids content of 15% to 30% (s
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Mon May 31 21:50:59 EDT 1999 | Dave F
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi