Electronics Forum | Mon Jul 16 10:44:29 EDT 2007 | Jacky
Hi All, Recently, we encountered strange defect at our SMT line. We can see solder ball spatter around at one of the component pad. This lead to insufficient solder defect at 1 side of the component. The other side of the component look good(Meet
Electronics Forum | Wed Jul 02 12:42:58 EDT 2003 | slthomas
Not sure how else to describe this. We've received some boards (1/2" x 3.5" x .0325" board built on panels of 24) with numerous resistors showing separation of the solder from the metallization at the top of the joint. There are 26 0805's on the bo
Electronics Forum | Tue Jan 21 13:51:19 EST 2014 | rgduval
Armando, Is the problem in the same spot on the board with every run? If so, there might be something about that particular location that is part of the cause (ie. ground or power plane connection). It sounds like you're seeing blow holes, or insu
Electronics Forum | Fri Apr 04 01:39:21 EDT 2008 | slthomas
All of what Dave says is spot on. I suspect that the most likely corresponding defects on your assemblies would be poor wetting and insufficient solder.
Electronics Forum | Tue Dec 14 10:36:42 EST 1999 | Paul Peterson
I recently encountered reflow soldering defects on a pair diode package, the smd pad had a green contamination, I'm convinced that this is not oxidation. The no-solder condition appears to be caused by a sloppy soldermask process, although over the y
Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT
Electronics Forum | Thu Oct 29 21:16:15 EDT 2009 | mah115
Fellows, We are considering getting an AOI machine to inspect boards that our vendors are giving us (we outsource the assembly of PCBAs). We have low volumes of boards, but every time a defect does slip by our human inspectors, it causes a lot of
Electronics Forum | Thu May 26 21:09:01 EDT 2005 | thaqalain
The reliability of a Gullwing component solder joint is in question when insufficient solder is evident: *at the heel of the lead *at the toe of the lead *none of the above
Electronics Forum | Fri Apr 29 14:16:16 EDT 2011 | ppcbs
Below is the long explanation. This defect is most commonly found with BGA components, but can arrise with all components. I see it happening more now with lead free boards that are being assembled with a no clean flux. Best short term remedy is t
Electronics Forum | Fri Sep 25 16:38:56 EDT 2009 | esoderberg
empf issued an excellent study of calculated solder volume in the 90's. It used lotus 123 but is easily used in excel. I have used it for over 10 years. The only thing wrong is with leadless components. the amount of paste required generally is insuf
.gif)