Electronics Forum | Wed May 23 10:11:43 EDT 2012 | blnorman
Simple answer is no, there is no universally acknowledged acceptance criteria. Some time ago, I started a spreadsheet with the acceptance levels suggested by various labs on the individual ionic species. All are relatively close in their individual
Electronics Forum | Wed Mar 08 14:11:38 EST 2006 | mholz
I am looking for an industry standard �stock� note to place on our printed circuit board assembly drawings that will capture a level of cleanliness for an IPC-A-610 class 2 board assembly. I�m looking for some quantitative spec for cleanliness that w
Electronics Forum | Tue Sep 03 17:48:34 EDT 2002 | dphilbrick
My customer is finding a blue haze on some SMT pads after processing, kind of looks like a water spot on the surface of solder joints. It requires 20x mag and very good lighting to see. We have done 2 different ionic tests and the boards pass to clas
Electronics Forum | Wed Aug 13 18:12:20 EDT 2003 | Carol
Has anyone tried to get conformal coating under a BGA? (large package MPC555). There is a concern with ionic/metal bridges developing between contacts due to accumulation of dust/humididty. Final product is Class 3 (aerospace). Thanks, Carol
Electronics Forum | Thu Sep 16 07:57:26 EDT 1999 | Seli
| | Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | | | I guess it depends what you mean by 'near'. Will the building be a custom design or an existing one? What kind of p
Electronics Forum | Mon Nov 01 13:25:29 EST 2004 | Dreamsniper
Hi Guys, Maybe you could help me with the above. We are doing IPC Class 3 products and would like to know more about the difference between the 2. We have an Omegameter, do we need an Ionograph too? Which one between the 2 is effective in Ionic Cont
Electronics Forum | Thu Sep 16 02:48:48 EDT 1999 | Brian
| Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | I guess it depends what you mean by 'near'. Will the building be a custom design or an existing one? What kind of product
Electronics Forum | Thu Sep 16 05:31:00 EDT 1999 | Earl Moon
| | Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | | | I guess it depends what you mean by 'near'. Will the building be a custom design or an existing one? What kind of p
Electronics Forum | Thu Sep 17 12:08:13 EDT 1998 | Graham Naisbitt
Wayne, I think Dave and Justin are correct but I would just add my twopennworth: Your customer presumably wants to know if the end-product will be reliable? If he/she wants you to prove cleanliness, ask them for the spec they want to work to and app
Electronics Forum | Fri Sep 17 04:49:10 EDT 1999 | Brian
| | | Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | | | | | I guess it depends what you mean by 'near'. Will the building be a custom design or an existing one? What kin
.gif)