Electronics Forum | Wed Feb 16 12:34:49 EST 2005 | greg
Hi all We recently have a problem with component in package 0805 (capasitor 100nF). I have noticed that after reflow soldering only one lead of the component is soldered. The second one is just laying on the PCB land. We use screen printing process
Electronics Forum | Thu Feb 17 04:09:19 EST 2005 | greg
The solder adheres to the lands very well so i don't think that problem is with solderability of the PCB. Not wetting to the 0805 terminations. When the problem appeared with the 0805 we chenged the supplier. But there was commnon element Pb-free te
Electronics Forum | Thu Jan 05 17:06:38 EST 2006 | russ
Is it now acceptable to discard the SAC alloy directly into the trash or is it still a requirement to dispose of through hazmat procedures. Seems to me that we can now just chuck the old paste right into the normal trash since it is the replacement
Electronics Forum | Sat Jul 28 08:37:52 EDT 2007 | davef
There is no good choice. Board Finishes: Industrial/Battelle Class 3 Environment [Reliability Knowledge Gaps: For use of Pb-free solders in High Reliability Applications, J Smetana, iNEMI Availability of SnPb-Compatible BGAs Workshop, March 1, 2007,
Electronics Forum | Thu Jul 26 23:57:47 EDT 2007 | gioblast
Good day.. anyone who have read the best guide on pb-free pcb plating?? I know immersion is the best but the storage controls sucks..easily changes color..ANYONE WITH A BETTER kNOWLEDGE ON HOW TO CONTROL? OR better plating ...enig?? why?? please. all
Electronics Forum | Sun Feb 01 07:50:07 EST 2009 | davef
The concern about lead contamination of lead-free solder has to with zone refining. For more, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=30315
Electronics Forum | Fri Jan 30 18:24:09 EST 2009 | gsala
Buenas dias Jos�, It shoul not be a problem. We had situation like that when in the early 2006 the Lead Free fase in Pb fase out, no pbm on solder joints. Today, after about 3 years, those cards are stil working in the field without any defect. Reg
Electronics Forum | Tue Feb 03 03:35:30 EST 2009 | sachu_70
Hi Jose, such a process is possible, but you need to confirm that the PCB material has high Tg. In additon, you need to re-look solder paste printing parameters and make required changes in stencil apperture design for optimum solder volume. Just a
Electronics Forum | Fri Jan 30 15:11:50 EST 2009 | joseluis_amper
Dear Sir. Recently we had a problem in our production. We had pcbs with no RoHs (with solder Pb in pads) but we used paste Lead Free. I want to know if we will have problems in this solders in the future, because (perhaps)the solder will be broken, o
Electronics Forum | Tue Feb 03 10:25:56 EST 2009 | milroy
Hi What is the surface finish you have? Following are true if you have HASL-LeadFree surface. I have had the same problem 3years ago and we did some micro-sectioning for further analysis, still the boards are functioning properly. But you have to
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830