Electronics Forum | Mon Jun 14 22:36:52 EDT 2004 | Ken
I hear ya Ray, but I have standard (automatic) solder dispenser that are 700gram modules. Jars have other issues that I have migrated away from... I like your idea of slaving the paste bar code label to the board scanner....
Electronics Forum | Tue Jun 01 19:42:46 EDT 2004 | Ken
The biggest fear is mixing the solder pastes and bar solder. Had a training program for teaching folks what the alloys are and how to read them. I have locked up the bar solder and use the buddy system to restock the pot. Put up many signs on le
Electronics Forum | Wed Dec 09 09:47:32 EST 2009 | dyoungquist
I am curious as to why you need to mix.... We use a 500g cartridge with air gun. Our process is remove the cartridge from the fridge, allow it to warm up to room temperature before inserting into air gun, then apply bead of paste to the stencil. N
Electronics Forum | Sat Oct 18 09:30:43 EDT 2008 | hussman
Sounds like a part problem. You can SOMETIMES over come this with a hotter profile. We see this a lot with brokered parts. Seems like a lot of people are rejecting parts because a lot of companies haven't perfected their RoHS process, yet produce
Electronics Forum | Tue Feb 03 03:35:30 EST 2009 | sachu_70
Hi Jose, such a process is possible, but you need to confirm that the PCB material has high Tg. In additon, you need to re-look solder paste printing parameters and make required changes in stencil apperture design for optimum solder volume. Just a
Electronics Forum | Sat Oct 18 20:35:25 EDT 2008 | arosario
I see, maybe changing my peak temp in reflow will help. I'll try do eval again... Actually, once I did have evaluated a longer pre-heat but on my previous eval, I didn't change the peak temp. Maybe reflow can help compensate to my problem in the part
Electronics Forum | Sun Feb 01 07:50:07 EST 2009 | davef
The concern about lead contamination of lead-free solder has to with zone refining. For more, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=30315
Electronics Forum | Fri Jan 30 18:24:09 EST 2009 | gsala
Buenas dias Jos�, It shoul not be a problem. We had situation like that when in the early 2006 the Lead Free fase in Pb fase out, no pbm on solder joints. Today, after about 3 years, those cards are stil working in the field without any defect. Reg
Electronics Forum | Fri Oct 17 22:36:35 EDT 2008 | arosario
Hi All, We just started build a new product and I am encountering many non-wet rejects in our new product. I need help on what should I look into to improve our Yield. Please see below back ground 1. We are using DEK Infinity as printer. 2. We are mo
Electronics Forum | Tue Jun 01 08:55:01 EDT 1999 | James Whitehouse
We have experienced problems with chlorine damaging certain components, is there anyone with similar problems and possible solutions ? preferably info about a source for chlorine free solder paste Thanks James