Electronics Forum | Thu Apr 27 21:00:32 EDT 2000 | Dave F
Scott: I�m not familiar with some of the things you�re talking about, but let me: * Agree with Russ & Peter regarding immersion silver. * Give some snips of information on the substrate side of things that might help you to tie this together. � FR-1
Electronics Forum | Thu Mar 23 22:26:53 EST 2006 | Joseph
Dear all, Referring comment from Mr. Jack,IPC director certification & assembly technology, the term "fillet tearing" is too broad. Cracks or fractures in the required fillet area, with SnPb or LF alloy and whether you call it tearing or not, is a D
Electronics Forum | Wed Aug 08 21:18:15 EDT 2001 | davef
Get-out the razor blades, bud. You could run that sukka for 6 sec dwell, cook breakfast on it, and you still will not get fill. [Hole file that is, breakfast will go along ways if peckish, though.] You could fire-up the depleted ozone rework gun [
Electronics Forum | Fri Aug 20 13:00:16 EDT 1999 | ScottM
| I'm trying a second time to post this very important message, to me, concerning Air-Vac's following creation. Does any own and use this stuff successfully to remove solder from 20 layer and up MLB's with .020" diameter holes? Also, is any of the ad
Electronics Forum | Mon Apr 01 19:57:07 EST 2002 | davef
Selective soldering machines are a good way to "finish automation", if the design of the PCB is conducive to the application with just a few components to solder. Your points are good. A decision matrix for selecting a machine might also include:
Electronics Forum | Thu Nov 06 09:10:13 EST 2003 | successmani
hi, NEMI recommends separate solders for reflow sodlering and wave soldering. Reflow soldering- Sn-3.9Ag-0.7Cu Wave sodlering- Sn-0.7CU Wavesoldering- Sn-0.7Ag What will happen if a mixed technolgy PCb board containing both through hole and surface
Electronics Forum | Tue Oct 16 21:53:15 EDT 2018 | reckless
http://www.aoisystems.com/ I was at the SMTA show and saw this company's booth. It looked like a good product at a good price but it doesn't do 3D AOI. The sales person was saying that 3D AOI is only useful in cases where a lead pin is hanging in
Electronics Forum | Thu Jun 04 09:25:21 EDT 1998 | Chrys
| | | Hello: | | | BACKGROUD: SMT components soldered on the top-side of boards that also require wave soldering have the potential to reflow during wave soldering. Reflowing these components during wave soldering is not good. It can cause cold jo
Electronics Forum | Wed Jun 03 21:40:38 EDT 1998 | Dave F
| | Hello: | | BACKGROUD: SMT components soldered on the top-side of boards that also require wave soldering have the potential to reflow during wave soldering. Reflowing these components during wave soldering is not good. It can cause cold joints
Electronics Forum | Thu Dec 03 21:40:01 EST 2020 | itmconsulting
Hey Kyle - Good for you for pushing your horizons and considering pin-in-paste (aka "Intrusive Soldering"). Don't let the nay-sayers out there discourage you. When I encounter mixed tech PCBAs (SMT and through-hole) my first choice, if the design a