Electronics Forum | Sat Nov 08 10:04:26 EST 2003 | severs
Once you have selected your plating based on electrical and physical requirments, you should know that there is an inexpensive plastic storage packaging developed by Lucent which can keep any platings solderability from degrading for up to 10 years o
Electronics Forum | Fri Nov 07 15:57:56 EST 2003 | Marc Simmel
Are there specifications or recommendations for electro-deposited tin-lead plating thickness on austenitic stainless steel that would provide a shelf life of 1 year? 6 months? Would 2 to 3 microns (78 to 118 micro-inches) 90/10 tin-lead over 1.27 mi
Electronics Forum | Thu Jan 29 09:18:36 EST 2015 | davef
Nichrome, manganin, phosphor bronze etc are easy to solder ... the hard part is removing the corrosion * Manganin: 86% copper, 12% manganese, 2% nickel. Often, it's used in making cryogenic measurements, due to its low heat loss. * Select a flux for
Electronics Forum | Mon Jan 07 11:58:06 EST 2008 | russ
they make tin plated steel batt contacts. may be your best option
Electronics Forum | Thu Jan 03 11:00:03 EST 2008 | patrickbruneel
As Dave said stainless steel can not be soldered using fluxes designed for electronics. The only way this could be done is to spot plate copper or tin where you want to make the solder connection.
Electronics Forum | Fri Jan 04 16:02:56 EST 2008 | fsw
All, The reason SS (stainless steel) was being considered is - customer wnats to reduce Ni or basically eliminate it. Anyway, seems that soldering SS for electronics is not going to be an easy option. Suggestions for different plating has been forwa
Electronics Forum | Thu Jul 24 12:36:54 EDT 2008 | rfematt
We have a new board that requires a membrane switch. The membrane switch is a 1" stainless-steel dome. We were wondering if ENIG plating will hold for an expected life
Electronics Forum | Thu Jan 03 17:39:34 EST 2008 | flipit
Why are you using stainless steel? Corrosion resistance? Can the stainless be gold plated? I think this can occur metallurgically. Maybe nickel first then gold. Why are you removing the nickel? Nickel is somewhat magnetic. Had an application onc
Electronics Forum | Mon Mar 29 21:19:38 EDT 2010 | mbclemens60
I have a customer that wants 5000 hrs to red rust. The steel is plated with chloride zinc (barrel plated) and a black chromate. They say a company in Taiwan has the technology, but can not deliver in a production setting. Does anyone know of a cost e
Electronics Forum | Wed Mar 11 16:43:20 EDT 2020 | sumote
There is a 8lb steel plate that is held down by 4 toggle bolts at the top of the machine. Its where you load the cutting media. If that plate does not have a pressure gauge built into it, contact CCR. They will send you one free of charge (at least t