Electronics Forum | Thu Jan 08 15:03:40 EST 2004 | dwzeek
We have an ongoing problem with our QFP144 packages soldering. It has not received much attention until late due to some customer failures. Most of the failures would show up in ESS testing and be repaired. The failure rate is about 2 in 1000 parts f
Electronics Forum | Sun Jun 22 13:24:49 EDT 2014 | davef
I don't know. We never had craziness like this before lead-free. You should have the yellowish-metal analyzed to be sure. Guessing: You're seeing this color on the terminations of components, not on the bulk of the SnX solder connection. If that's
Electronics Forum | Mon Dec 16 15:10:56 EST 2002 | Randy Villeneuve
We do not bake any of our boards prior to wave solder. If we did we would have one heck of a large oven. I would assume you are concerned about moisture sensitive components. In most cases your top side parts should only get to 80 degrees centigarde
Electronics Forum | Tue Aug 18 02:10:14 EDT 2009 | sergey2007
Hello, I have a customer who recentely installed a vapor phase soldering system. Everything goes pretty well, but from time to time the customer has the same problem with the soldering: one of the components on PCB (usually, it's a QFP package) is ro
Electronics Forum | Mon Jul 26 10:25:12 EDT 1999 | Boca
| | We are having a process related problem with pullup resistors on a controller card which has a I960 micro-processor. | | The controller monitors signal inputs and it's own resources then blinks a LED to indicate its working. The problem is that a
Electronics Forum | Mon Jul 26 14:14:51 EDT 1999 | Steve Gregory
| | | We are having a process related problem with pullup resistors on a controller card which has a I960 micro-processor. | | | The controller monitors signal inputs and it's own resources then blinks a LED to indicate its working. The problem is th
Electronics Forum | Wed Aug 10 10:41:23 EDT 2005 | patrickbruneel
Bob, Great theory if you're selling SN100C, but I have to disagree that an alloy being 4�C off eutectic will cause cracks. When a solder joint exits the solder wave, there is an immediate drop in temperature of 100�C. so being off 4�C is irrelevant.
Electronics Forum | Thu Jul 15 18:07:04 EDT 2004 | dwanzek
This has been a tough one to date. Any ideas will help. Problem definition � random QFP144 part not soldering all leads. Percentage fallout is about 1-5% of boards. Usually leads, one or more, on trailing side to the direction of travel does not wet
Electronics Forum | Wed Dec 17 03:26:17 EST 2003 | Kev
Hi Lads, Thanks for all of the replies. To answer a few of your questions..... My wave is a Hollis PT500N. It has 3 zones of pre-heater rod elements. Each individual element (601195-01) is 500 watts. There are 16 elements per zone so 8 Kw per zone.
Electronics Forum | Mon Dec 06 05:18:53 EST 1999 | Wolfgang Busko
Hi Russ, assuming that only your flux changed and the PCB-finish stayed the same it seems to me that the solderability of that finish is somehow poor. About Ni/Au it can be said that the solderconnection is made between Ni and Sn. The Au-finish is ju
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830