Electronics Forum | Thu Aug 13 07:53:40 EDT 1998 | Earl Moon
| | Couple of questions. | | 1) Are we talking alumina substrates as the ceramic material? | | 2) Are we co-firing gold as the conductors on the substrate surface? | | 3) In other words, is this a hybrid thick film circuit? | | 4) If so, how large or
Electronics Forum | Fri Aug 14 07:27:42 EDT 1998 | Earl Moon
| | Hi, can you please tell me how to make green coating and through-hole plating of PCB? Thanks! | | Xingsheng | Xingsheng: Welcome. | Bible on PCB fabrication: Printed Circuits Handbook, Clyde Coombs, McGraw-Hill | Web resources: http://www.pw
Electronics Forum | Fri Aug 14 08:59:51 EDT 1998 | Dave F
| | | Hi, can you please tell me how to make green coating and through-hole plating of PCB? Thanks! | | | Xingsheng | | Xingsheng: Welcome. | | Bible on PCB fabrication: Printed Circuits Handbook, Clyde Coombs, McGraw-Hill | | Web resources: htt
Electronics Forum | Wed Jan 12 10:05:20 EST 2005 | Dreamsniper
we are using polyimide boards 6 inches x 7 inches, 2.5mm thick, 12 to 14 layers, for aerospace industries. I am using a long bake of 12 hours at 70'C prior to manufacturing or exposure to elevated reflow and wave soldering temperature. If schedule i
Electronics Forum | Thu Aug 01 13:04:57 EDT 2002 | gdstanton
Its interesting. It appears I'm getting conflicting feeback from Indium. This says its not a problem... http://indium.custhelp.com/cgi-bin/indium.cfg/php/enduser/std_adp.php?p_sid=kTDKGClg&p_lva=&p_faqid=355&p_created=1014734692&p_sp=cF9ncmlkc29
Electronics Forum | Fri Apr 03 08:34:54 EDT 2020 | SMTA-Gregory
We need to be careful with product to avoid introducing a new failure mode, namely corrosion and dendrite growth, especially those running no clean processes! In addition to heat (reflow, wave and some selective soldering processes) killing the vi
Electronics Forum | Mon Jun 27 09:09:19 EDT 2005 | Bob R.
We've all been soldering Pb free parts for a couple decades. All your surface mount capacitors have probably had a Sn finish for years. Whenever one of our parts with a SnPb finish converts for Pb free we have the manufacturing site do a small buil
Electronics Forum | Mon Jun 27 14:20:57 EDT 2005 | Bob R.
If you visually inspect the solder joints of the first dozen or so boards with the Pb free parts and you're meeting workmanship standards then I wouldn't worry about it. When we started getting the first barrage of Pb free parts a couple years ago w
Electronics Forum | Wed May 27 14:35:52 EDT 1998 | Justin Medernach
| | R&D is currently designing a board with smt components on both sides of the board. They are adding a 16 pin IC Gull wing. on the bottom side of the board. I have asked for only caps and resistors to be placed on the bottom side. Is there a recomm
Electronics Forum | Mon May 22 11:29:45 EDT 2017 | rbickle
Hey all, We are a small electronics manufacturing company who has been using the solder reflow process for years, but we have been hand placing components. We only run the system 2-3 days per week. I have been looking at buying a used pick and pla