Electronics Forum | Mon Nov 07 12:25:32 EST 2005 | Rob
Hi CW, Larger chip caps can be susceptable to cracking, but mainly this is due to handling - flexing of boards is the main culprit (the part being mechanically joined at both ends to the board). PCB's usually flex easiest along one axis, and larger
Electronics Forum | Mon Nov 07 16:31:47 EST 2005 | CW
hi Bob, Thanks for the info. I understand your comments, but I am looking for specific guidance, If I am putting chip capacitors on a .063 FR4 board, what size package should we stay away from to avoid cracking? (I realize this is dependent on h
Electronics Forum | Tue Apr 26 11:22:48 EDT 2005 | denismeloche
I have found that Sn62 solder gives better strength and leach resistance when soldering to gold surfaces. The gold needs to be at least 5 to 10 micro inches thick to prevent nickel oxidation but if over 25 micro inches will cause brittleness. I hav
Electronics Forum | Mon Oct 28 07:07:39 EST 2002 | cyber_wolf
It has been my experience that when all conditions are as they are supposed to be there should be zero or very little deflection. When you start placing components with pick and place equipment that does not have a Z pressure sense, you run the possi
Electronics Forum | Wed Oct 30 01:23:22 EST 2002 | jasper
It has been my experience that when all > conditions are as they are supposed to be there > should be zero or very little deflection. When > you start placing components with pick and place > equipment that does not have a Z pressure sense, > yo
Electronics Forum | Tue Oct 09 20:27:13 EDT 2001 | davef
That�s a 672 BALL BGA, bud!!! It�s a BIG Mutha!!! [I know. I know. For some reason suppliers call balls "pins".] Let�s focus on: * Clarifying the units on your PCB and aluminum plate thickness measurements. * Describing your use of the aluminum pl
Electronics Forum | Mon Oct 08 23:17:48 EDT 2001 | Brad Arnold
We are trying to produce a PC Card bus assembly with a 672 pin BGA on one side. These pcb's are .015 thick. I believe the ball pitch is .5mm. The pcb's are plated with white tin. The pcb's are in a 1 X 3 array. We had 2 plates with appropriate cutout
Electronics Forum | Thu Oct 11 17:44:30 EDT 2001 | aaelect
OK, OK. 672 ball BGA. The pcbs are PC Card bus size and are .015 thick. There are 3 on a panel with about 1/2" between and rails. The aluminum plates are about 3" by 7". There are 3 cutouts which allow for the parts from either side to protrude du
Electronics Forum | Thu Oct 11 22:25:50 EDT 2001 | davef
Bruce I�m with yall. Designers and fabricators say �pins�. You say: * BGA pins are 1mm [0.039�] pitch. * BGA pads are 0.4mm [0.0157�] diameter. * BGA pins are 0.6 mm [0.024�] side-to-side. * Board thickness is ~0.4 mm [0.015�] First, as you can
Electronics Forum | Mon May 13 23:44:26 EDT 2019 | dami0629
if use tray cannot solve the problem, you can change from the design 1)Reduce the effect of temperature on PCB 2) PCB USE HIGH TG 3) BOARD THICKNESS TOO THIN 4) MODIFY THE BOARD SIZE 5) Reduce the V-CUT depth.
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830