Electronics Forum | Tue Aug 15 16:57:54 EDT 2000 | Doug Philbrick
In many threads here I have read and talked about Electroless Gold problems and have experienced my own problems with it. Love to hear what others are doing as a replacement. Is it Electroless tin, is it osp or is HASL good enough for .031 pitch BGA
Electronics Forum | Fri Jul 21 12:28:02 EDT 2000 | Barbara Keating
MVT has never been in as strong position as they are today. Over the past two weeks alone, MVT has opened two new offices in Mexico and Singapore, launched new products and closed more sales than any other previous period. MVT's AOI solutions are rap
Electronics Forum | Fri May 05 18:51:59 EDT 2000 | Steve Thomas
Looking for the best choice in books on soldering processes, primarily reflow but wave is going to be with us for a while so..... If you had to buy one today, which would you start with? Here's the list I gleened from the archives: Coombs, CF, "Pr
Electronics Forum | Tue Mar 13 18:25:45 EST 2001 | slthomas
Anyone doing a print-dispense-place-reflow process? I've never heard of it being done this way before today. Don't know why, actually, as it sounds like a fairly friendly method provided the adhesives used are happy with a standard reflow profile.
Electronics Forum | Tue Aug 22 14:59:55 EDT 2000 | Mike Naddra
What does the reflow profile look like , the question I had was surrounding the higher reflow temperature and the max temperature that lowest thermal mass components will see. Some other questions that I had were surrounding the components , what of
Electronics Forum | Thu Jul 20 14:05:59 EDT 2000 | Mike McMonagle
With 0402 components becoming more common today outside of the telecommunications industry, our company is qualifying equipment and processes for an upcoming product incorporating 0402s. Having used 0402s in a previous position, I am planning a DOE o
Electronics Forum | Wed Jun 13 21:33:34 EDT 2001 | davef
Todays crazy idea?! (environmental safe) February 22, 2001 05:33 AM Mattias Andersson [http://www.smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&&Message_ID=5343&_#Message5343] Turning things just a bit, our working theory is: burnt flux
Electronics Forum | Fri Jul 13 01:34:13 EDT 2001 | dlkearns1
Quick update on my issue of " wicking ". I had some talk with the company QA guy. Told him I saw no wicking on the test panels at 30X. The next day he came up to me and said, he kinda saw a little something at 60X then verified that at 100X, So, he
Electronics Forum | Fri Dec 03 14:33:18 EST 1999 | John Thorup
Hi Cunli I guess it's too much to hope for that you're back but it's nice that you're still paying attention . I've used the printer friendly version before and it worked fine. However it does't always work. I'm holding Dave F's posting (help with
Electronics Forum | Fri Sep 03 14:20:38 EDT 1999 | David
| Could someone shares their experience on the causes of 'Open' in the BGA after reflow. | | You must have been in the same meeting I was in earlier today. We are currently having some opens on BGAs. The problem joints are all on the perimeter of