Electronics Forum | Wed Feb 20 19:57:27 EST 2002 | davef
THIEVING * Layout: I�d guess the surface area of your thieves is not large enough. The pull from the thief is not great enough to over-come the pull from the connector pins and pads. Consider tripling the size of the thief. As you say, reducing t
Electronics Forum | Sun Oct 20 19:42:29 EDT 2002 | sjpence
Like Russ, I am also curious about the 100% fill requirement. On any thick, high mass board the key is getting as much heat as possible into the board. If you get the board to the proper temperature, solder will flow just about anywhere. As an alte
Electronics Forum | Tue Mar 28 11:17:19 EST 2006 | smartasp
Thanks for the input Guys Yeah the not so knowledgable customer does not like to residues for cosmetic resons. The flux is for lead free process, of the no clean and water soluable type. We have explained to him that technically the residues do not
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Sat Jun 05 00:27:54 EDT 1999 | Dean
| | | To you all for comment and summary, | | | | | | The following things I like without endorsing (PCB/PCBA stuff - outside the great women in my life [many] and without [mostly]): | | | | | | 1) A good set of design rules | | | 2) A good set of
Electronics Forum | Thu Jun 03 07:10:31 EDT 1999 | Earl Moon
| | To you all for comment and summary, | | | | The following things I like without endorsing (PCB/PCBA stuff - outside the great women in my life [many] and without [mostly]): | | | | 1) A good set of design rules | | 2) A good set of design rules
Electronics Forum | Tue Jan 25 14:25:47 EST 2000 | Mark Miller
Has any one experienced hand soldering through hole components to white tin plated PCB's using no-clean wire solder? Our facility is presently evaluating white tin vs Sn/Pb coatings. Our only difficulty at this time has been hand soldering of wires
Electronics Forum | Thu Apr 20 08:49:08 EDT 2006 | Chunks
a) Is there a recommended dip or dwell time for the dip soldering? Check your data sheet for the part. Dwell time is everything in selective soldering. Top side wetting is a good process indicator. b) How do we improve the solder coverage in the
Electronics Forum | Mon Jun 11 17:47:54 EDT 2012 | tombstonesmt
Pete B *We do lines of soldering @ 10mm/sec *Similar solder balls were present on product after soldering. *UPDATE SOLUTION* We began using topside preheat while fluxing the board to reduce the thermal shock factor in addition to replacing the "fi
Electronics Forum | Tue Oct 16 11:51:26 EDT 2001 | bobm
i am using the epibond. i had alpha come in and look at our set up. they told me that the epibond can be reflowed at regular temp profiles with no problems. because i only have one oven and two pick n place machines it was important to be able to run
A dealer of high quality Used SMT Equipment, Used Plastic Injection Molding Equipment, Used Machine Tools, Used Semiconductor Machinery, and Used Industrial Machinery.