Technical Library | 2014-11-18 23:59:30.0
Performance degradation of packaging material is an important reason for the lifetime reduction of LED. In order to understanding the failure behavior of packaging material, silicone and phosphor were chosen to fabricate LED samples within which an aging test at 125℃ was performed. The result of online luminance measurement showed that LED samples with both silicone and phosphor had the highest luminance decay rate among all test samples because the carbonization of silicone and the consequent outgassing reduced the luminance quickly. The result of the luminance variance with test time was analyzed and an exponential decay model was developed with which the lifetime of LED under high temperature could be estimated.
Technical Library | 2015-10-01 16:12:51.0
Solder paste printing is known to be one of the most difficult processes to quality assure in electronic manufacturing. The challenge increases as the technology development moves toward a mix between large modules and small chip components on large and densely populated printed circuit boards. Having a process for quality assurance of the solder paste print is fast becoming a necessity.This article describes a method to ensure quality secured data from both solder paste printers and inspection machines in electronic assembly manufacturing. This information should be used as feedback in order to improve the solder paste printing process.
Technical Library | 2018-08-22 14:05:42.0
Glass substrates are emerging as a key alternative to silicon and conventional organic substrates for high-density and high-performance systems due to their outstanding dimensional stability, enabling sub-5-µm lithographic design rules, excellent electrical performance, and unique mechanical properties, key in achieving board-level reliability at body sizes larger than 15 × 15 mm2. This paper describes the first demonstration of the board-level reliability of such large, ultrathin glass ball grid array (BGA) packages directly mounted onto a system board, considering both their thermal cycling and drop-test performances.
Technical Library | 2008-12-03 19:39:00.0
This paper presents the analysis from a recent printing study employing a test vehicle that includes components such as 01005s to QFPs. In a recent publication, part of this study was presented focusing on 01005 printing only. This printing process was determined to be suitable for 01005s assembly and also analyzed based on statistical capability. The current paper will present the results from additional detailed analysis to determine if this process has the capability to provide sufficient solder paste deposits for larger components located on the same test board. In the future, the SMT industry may always look towards “Broadband Printing” as an alternative to dual stencil or stepped stencil printing technologies in order to meet the needs of both small and large components.
Technical Library | 2009-09-18 14:52:06.0
Electronic assembly cleaning processes are becoming increasingly more complex because of global environmental mandates and customer driven product performance requirements. Manufacturing strategies today require process equivalence. That is to say, if a product is made or modified in different locations or processes around the world, the result should be the same. If cleaning is a requirement, will existing electronic assembly cleaning processes meet the challenge? Innovative cleaning fluid and cleaning equipment designs provide improved functionality in both batch and continuous inline cleaning processes. The purpose of this designed experiment is to report optimized cleaning process parameters for removing lead-free flux residues on populated circuit assemblies using innovative cleaning fluid and batch cleaning equipment designs.
Technical Library | 2012-11-15 23:38:50.0
First published in the 2012 IPC APEX EXPO technical conference proceedings. As we progress in the 21st century, electronics manufacturing will need more and more precision. Parts will get more complex since more components have to be assembled in smaller spaces. Circuit boards and other electronic assemblies will become more densely populated; spacings between components will be shorter. This will require precision manufacturing and efficient cleaning during and post manufacturing. In addition, with population and technology progressing, larger amount of greenhouse gases will be emitted resulting in higher global warming. Intense research effort is going on to develop new generation of chemicals to address both cleaning and global warming issues. Low global warming solutions in refrigeration and as insulating agents are already in the marketplace.
Technical Library | 2013-01-03 20:27:54.0
Electronics assemblies with large flip-chip BGA packages can be prone to either pad cratering or brittle intermetallic (IMC) failures under excessive PCB bending. Pad cratering cracks are not detected by electrical testing or non-destructive inspection methods, yet they pose a long term reliability risk since the cracks may propagate under subsequent loads to cause electrical failure. Since the initiation of pad cratering does not result in an instantaneous electrical signature, detecting the onset of this failure has been challenging. An acoustic emission methodology was recently developed by the authors to detect the onset of pad cratering. The instantaneous release of elastic energy associated with the initiation of an internal crack, i.e., Acoustic Emission (AE), can be monitored to accurately determine the onset of both pad cratering and brittle intermetallic (IMC) failures.
Technical Library | 2014-06-23 14:50:52.0
It was unusual to see chip terminations change colors when tin lead solders were used but with the introduction of lead free reflow soldering and the corresponding increases in reflow temperatures terminations are now changing colors. Two conditions are present when reflow temperatures are increased for lead free solder alloys that leads to discoloration. Reflow temperatures are above the melting point of tin (Sn MP is 232oC). Air temperatures commonly used in forced convection reflow systems are high enough to both melt the tin plating on the termination allowing it to be pulled into the solder joint due to solder joint liquid solder surface tension leaving behind the exposed nickel barrier. Now those metal oxide colors will be visible due to high air temperatures during reflow.
Technical Library | 2014-09-18 16:48:26.0
Two major drivers in electronic industry are electrical and mechanical miniaturization. Both induce major changes in the material selection as well as in the design. Nevertheless, the mechanical and thermal reliability of a Printed Circuit Board (PCB) has to remain at the same high level or even increase (e.g. multiple lead-free soldering). To achieve these reliability targets, extensive testing has to be done with bare PCB as well as assembled PCB. These tests are time consuming and cost intensive. The PCBs have to be produced, assembled, tested and finally a detailed failure analysis is required to be performed.This paper examines the development of our concept and has the potential to enable the prediction of the lifetime of the PCB using accelerated testing methods and finite element simulations.
Technical Library | 2015-02-12 13:32:52.0
Market forces, particularly legislation against the use of lead in electronics, have driven electronics manufacturers towards lead-free solders for PCB assembly and rework. This approach creates challenges because of the relatively high temperatures needed for lead-free soldering. Additionally, lead-free solder alloys typically do not wet or wick as easily as Sn63Pb37 leaded types. As PCBs often include both BGAs and simpler discrete devices, a lead-free rework capability should include a suitable soldering station and a BGA rework station. This article shows how such equipment can be adapted to overcome the lead-free issues and provide a successful reworking facility.