Technical Library | 2019-06-03 15:32:40.0
ACI Technologies was pleased to assist a customer by conducting elemental analysis on several assemblies displaying severe corrosion. Several board assemblies had failed in the field and exhibited areas of corrosion in close proximity to onboard components. The most common source of corrosion on electronic assemblies is residual flux. Fluxes are specific chemistries applied during the soldering process which improve the wetting of the solder to both the pad and component when forming the solder joint. They can be highly reactive chemicals that, if left on the assemblies, can lead to corrosion, electrical degradation, and decreased reliability. In the presence of moisture and electrical bias, flux residue can enable dendritic growth as a result of electrochemical migration (ECM).
Technical Library | 2009-10-14 21:17:47.0
Electrochemical migration (ECM) is defined as the growth of conductive metal filaments across a printed circuit board (PCB) in the presence of an electrolytic solution and a DC voltage bias. ECM, also known as dendritic growth, is a critical issue in the electronics industry because the intermittent failure behavior of ECM is a likely root-cause of the high occurrence of field failures identified as no trouble found (NTF)/could not duplicate (CND)
Technical Library | 2022-03-16 19:48:18.0
Dendrites, Electrochemical Migration (ECM) and parasitic leakage, are usually caused by process related contamination. For example, excess flux, poor handling, extraneous solder, fibers, to name a few. One does not normally relate these fails with environmental causes. However, creep corrosion is a mechanism by which electronic products fail in application, primarily related to sulfur pollution present in the air.1 The sulfur reacts with exposed silver, and to a lesser extent, exposed copper. This paper will explore various aspects of the creep corrosion chemical reaction
Technical Library | 2021-07-27 14:54:26.0
Fast forward to current time. Today, our society embraces cleanliness. We expect, demand, and evaluate cleanliness in almost every aspect of our lives. We wash our cars and pets. We maintain high cleanliness standards in our hotels and public spaces. We require cleanliness in our restaurants and hospitals. We sanitize our hands throughout the day to prevent illness. We live in a clean-centric culture. While we drive clean cars, stay in clean hotels and eat clean food, there is one part of our life where we actually abandoned cleanliness. Many of the circuit assemblies that affect almost every aspect of our daily lives are no longer required to be clean. Even though our life experience confirms the link between cleanliness and reliability, happiness, health, and safety, circuit assemblies no longer maintain that "cleanliness is next to Godliness" status. This was not always the case. There was a time when virtually all circuit assemblies were cleaned. The removal of flux and other process-related contamination was commonplace. Cleaning was as normal as soldering. As we bring history into current time, one may relate the fall of Rome and its adoption of personal hygiene and the subsequent decline in human health to the large-scale abandonment of cleanliness expectations of circuit assemblies and the subsequent reliability issues it has created. How did this happen? Has history repeated itself?
| 1 |