Technical Library | 2013-08-29 19:52:43.0
Au over Ni on Cu is a widely used printed circuit board (PCB) surface finish, under bump metallization (UBM), and component lead metallization. It is generally accepted that less than 3 wt.% Au in Sn-Pb solder joints inhibits formation of detrimental intermetallic compounds (IMC). However, the critical limit for Au content in Pb-free solder joints is not well established. Three surface-mount package platforms, one with a matte Sn surface finish and the others with Ni/Au finish, were soldered to Ni/Au-finished PCB using Sn-3.0Ag 0.5Cu (SAC305) solder, in a realistic manufacturing setting. The assembled boards were divided into three groups: one without any thermal treatment, one subjected to isothermal aging at 125°C for 30 days, and the third group aged at 125°C for 56 days...
Technical Library | 2012-10-18 21:58:51.0
First published in the 2012 IPC APEX EXPO technical conference proceedings. In this paper, we report on a comprehensive study regarding the morphology evolution and voiding of SnAgCu solder joints on the central pad of two different packages – QFN and an Agilent package called TOPS – on PCBs with a Ni/Au surface finish.
Technical Library | 2012-12-13 21:20:05.0
First published in the 2012 IPC APEX EXPO technical conference proceedings. We investigated the micro-void formation of solder joints after reliability tests such as preconditioning (precon) and thermal cycle (TC) by varying the thickness of Palladium (Pd) in Electroless Nickel / Electroless Palladium / Immersion Gold (ENEPIG) surface finish. We used lead-free solder of Sn-1.2Ag-0.5Cu-Ni (LF35). We found multiple micro-voids of less than 10 µm line up within or above the intermetallic compound (IMC) layer. The number of micro-voids increased with the palladium (Pd) layer thickness. Our results revealed that the micro-void formation should be related to (Pd, Ni)Sn4 phase resulted from thick Pd layer. We propose that micro-voids may form due to either entrapping of volatile gas by (Pd, Ni)Sn4 or creeping of (Pd, Ni)Sn4.
Technical Library | 2017-02-28 12:39:50.0
During the last 5 years mobile phones and other portable consumer electronics have been extremely popular and spread all over the world in different climate zones in very high volumes. At the same time the mobile phone terminal for many people has become a necessity that is brought with them in any activity they practice. These changes in user behavior have heavily changed the impact on handheld terminals from moisture, sweat, corrosive atmospheres and mechanical drop. As a result of this the requirement to solder joint reliability, corrosion stability and wear resistance are heavily increasing to keep a high reliability of the terminal.Immersion Ni/Au has been the overall dominant surface finish on Printed Wiring Boards (PWB's) for the last 10 years, but a paradigm shift to avoid use of this thin and porous surface finish is ongoing nowadays because it can’t address these challenges in a satisfactory way.In today's handheld terminals, Organic Solder Preservative (OSP) has replaced Immersion Ni/Au on solder pads. Carbon surface finish for Key- and spring contact-pads, combined with the right concept design can make use of Immersion Ni/Au unnecessary in the near future. The result will be higher reliability with less expensive and simpler processes.This paper will discuss the various considerations for choice of surface finish and results from the feasibility studies performed.
Technical Library | 2023-08-04 15:27:30.0
A designed experiment evaluated the influence of several variables on appearance and strength of Pb-free solder joints. Components, with leads finished with nickel-palladium-gold (NiPdAu), were used from Texas Instruments (TI) and two other integrated circuit suppliers. Pb-free solder paste used was tin-silver-copper (SnAgCu) alloy. Variables were printed wiring board (PWB) pad size/stencil aperture (the pad finish was consistent; electrolysis Ni/immersion Au), reflow atmosphere, reflow temperature, Pd thickness in the NiPdAu finish, and thermal aging. Height of solder wetting to component lead sides was measured for both ceramic plate and PWB soldering. A third response was solder joint strength; a "lead pull" test determined the maximum force needed to pull the component lead from the PWB. This paper presents a statistical analysis of the designed experiment. Reflow atmosphere and pad size/stencil aperture have the greatest contribution to the height of lead side wetting. Reflow temperature, palladium thickness, and preconditioning had very little impact on side-wetting height. For lead pull, variance in the data was relatively small and the factors tested had little impact.
Technical Library | 2024-04-08 15:46:36.0
A designed experiment evaluated the influence of several variables on appearance and strength of Pb-free solder joints. Components, with leads finished with nickel-palladium-gold (NiPdAu), were used from Texas Instruments (TI) and two other integrated circuit suppliers. Pb-free solder paste used was tin-silver-copper (SnAgCu) alloy. Variables were printed wiring board (PWB) pad size/stencil aperture (the pad finish was consistent; electrolysis Ni/immersion Au), reflow atmosphere, reflow temperature, Pd thickness in the NiPdAu finish, and thermal aging. Height of solder wetting to component lead sides was measured for both ceramic plate and PWB soldering. A third response was solder joint strength; a "lead pull" test determined the maximum force needed to pull the component lead from the PWB. This paper presents a statistical analysis of the designed experiment. Reflow atmosphere and pad size/stencil aperture have the greatest contribution to the height of lead side wetting. Reflow temperature, palladium thickness, and preconditioning had very little impact on side-wetting height. For lead pull, variance in the data was relatively small and the factors tested had little impact.
Technical Library | 2014-01-09 16:40:33.0
Embedded Passive Technology is a viable technology that has been reliably used in the defense and aerospace industry for over 20 years. Embedded Passive (Resistors and Capacitors) Technology have a great potential for high frequency and high density applications. It also provides better signal performance, reduced parasitic and cross talk. This paper summarizes the selection of resistor embedded materials, evaluations of resistive material (Phase 1) and duplication of a complex digital design (Phase 2). Phase 1 –resistive materials (Foil 25Ω/sq NiCr and 1kΩ/sq CrSiO) and resistive-Ply materials (25Ω/sq and 250Ω/sq NiP) were chosen for evaluation.
Technical Library | 2017-06-01 17:12:08.0
The corrosion of Nickel-Palladium-Gold (Ni-Pd-Au) finish terminals in humid environments is known to be reduced with the application of a conformal coating such as acrylic. Corrosion has a higher rate of occurrence around the terminal ‘knee’ of a surface mount component, which may be reduced with the application of conformal coatings. Although radio frequency (RF) plasma processing is generally known to enhance conformity of conformal coating to surfaces through ionic bombardment, the effect on the functionality of assembled printed circuit boards (PCB) is not as well known. The purpose of this study is to assess whether RF plasma processing can enhance the adhesive and coverage qualities of an acrylic conformal coating on PCBs, specifically on Ni-Pd-Au terminals with a knee, and if plasma processing has an effect on the electrical functionality of components and fully assembled PCB.
Technical Library | 2021-12-29 19:52:50.0
Medtronic seeks to quantify the thermal aging limits of electroless Ni-electroless Pd-immersion Au (ENEPIG) surface finishes to determine how aggressive the silicon burn-in process can be without loss of solderability. Silicon burn-in (power testing at elevated temperature) is used to eliminate early field failures, critical for device reliability. Thermal aging due to burn-in or annealing causes Ni and Pd diffusion to and oxidation on the surface. Surface oxides limit wetting of the PbSn solder, affecting electrical connectivity of components soldered afterburn-in. Isothermal aging of two ENEPIG surface finishes was performed at 75°C-150°C for 100 hrs-1500hrs to test the thermal aging limits and identify how loss of solderability occurs.
Technical Library | 2022-03-02 21:26:51.0
The solderability of a nickel-palladium-gold (Ni-Pd-Au) finish on a Cu substrate was evaluated for the Pb-free solder, 95.5Sn-3.9Ag-0.6 Cu (wt.%, abbreviated Sn-Ag-Cu) and the eutectic 63Sn-37 Pb (Sn-Pb) alloy. The solder temperature was 245ºC. The flux was a rosin-based mildly activated (RMA) solution. The Ni-Pd-Au finish was tested in the as-fabricated condition as well as after exposure to one of the following accelerated storage (shelf life) regiments: (1) 33.6, 67.2, or 336 hours in the Battelle Class 2 flowing gas environment or (2) 5, 16, or 24 hours of steam aging (88ºC, 90%RH).