Technical Library | 2021-08-25 16:34:37.0
As the traditional eutectic SnPb solder alloy has been outlawed, the electronic industry has almost completely transitioned to the lead-free solder alloys. The conventional SAC305 solder alloy used in lead-free electronic assembly has a high melting and processing temperature with a typical peak reflow temperature of 245ºC which is almost 30ºC higher than traditional eutectic SnPb reflow profile. Some of the drawbacks of this high melting and processing temperatures are yield loss due to component warpage which has an impact on solder joint formation like bridging, open defects, head on pillow.
Technical Library | 1999-05-09 14:14:51.0
With the ongoing concern regarding environmental pollutants, Iead is being targeted in the electronic assembly arena. This paper highlights lead-free solders and the different combinations of elemental makeups.
Technical Library | 2012-07-05 06:10:59.0
First published in the 2012 IPC APEX EXPO technical conference proceedings. A new innovation for increasing quality & productivity of wave soldering machines.
Technical Library | 2012-08-30 21:24:29.0
This paper provides definitions of the different voiding types encountered in Gull Wing solder joint geometries. It further provides corresponding reliability data that support some level of inclusion voiding in these solder joints and identifies the final criteria being applied for certain IBM Server applications. Such acceptance criteria can be applied using various available x-ray inspection techniques on a production or sample basis. The bulk of supporting data to date has been gathered through RoHS server exempt SnPb eutectic soldering operations but it is expected to provide a reasonable baseline for pending Pb-free solder applications.
Technical Library | 2015-10-01 16:12:51.0
Solder paste printing is known to be one of the most difficult processes to quality assure in electronic manufacturing. The challenge increases as the technology development moves toward a mix between large modules and small chip components on large and densely populated printed circuit boards. Having a process for quality assurance of the solder paste print is fast becoming a necessity.This article describes a method to ensure quality secured data from both solder paste printers and inspection machines in electronic assembly manufacturing. This information should be used as feedback in order to improve the solder paste printing process.
Technical Library | 2021-09-08 13:57:37.0
While the presence of silver in SAC solder provided excellent temperature cycling durability, the silver in high silver SAC alloy also made the solders susceptible to failures under drop/shock loading. To improve the drop/shock reliability, the silver content in SAC alloys was reduced from three percent, to as low as no silver. Solder dopants, also known as microalloy additions, are elements (typically 0.1% or lower) other than the main constituents of the alloy that have been shown to improve solder performance. Commonly used microalloy additions include nickel (Ni), bismuth (Bi), manganese (Mn), and antimony (Sb).
Technical Library | 2007-12-20 16:28:08.0
Despite much research and discussion on the subject of reflow profiling, many questions and a good deal of confusion still exist. What is clear is that the pains often associated with profiling can be reduced if there is a strong understanding of the variables that can be encountered during the reflow process, as well as the metallurgical dynamics of the soldering process. This paper shall provide a brief outline of the reflow profile in general, with specific emphasis placed upon the suggested time spent above the melting temperature of the solder. The guidelines for soldering to various surfaces and with alternative solder alloys also are discussed.
Technical Library | 2009-11-05 11:17:32.0
Head-in-pillow (HiP), also known as ball-and-socket, is a solder joint defect where the solder paste deposit wets the pad, but does not fully wet the ball. This results in a solder joint with enough of a connection to have electrical integrity, but lacking sufficient mechanical strength. Due to the lack of solder joint strength, these components may fail with very little mechanical or thermal stress. This potentially costly defect is not usually detected in functional testing, and only shows up as a failure in the field after the assembly has been exposed to some physical or thermal stress.
Technical Library | 2016-11-17 14:58:02.0
Since 2006 RoHS requirements have required lead free solders to take the place of tin-lead solders in electronics. The problem is that in some environments the lead free solders are less reliable than the older tin-lead solders. One of the ways to solve this problem is to corner stake, edge bond or underfill the components. When considering what mitigation technique and material to use, the operating conditions must be characterized. The temperature range is important when selecting a material to use since the glass transition temperature (Tg) and coefficient of thermal expansion (CTE) are important properties. If improperly chosen, the mitigation material can cause more failures than an unmitigated component.
Technical Library | 2007-01-31 14:10:17.0
This white paper is suitable for both new and experienced users. It is a practical education in the use and misuse of auger valves for solder paste dispensing.