Electronics Forum | Fri May 31 05:54:09 EDT 2019 | dhanish
What are the common cause for solder joint crack after the pcba go through Temperature cycling test ?We have seen failure on solder joint for the memory part.
Electronics Forum | Tue Jun 25 09:45:39 EDT 2019 | edhare
See also ... https://www.semlab.com/solder-joint-failure-modes/
Industry News | 2010-04-30 18:47:15.0
SMTA China announces that it presented awards for the 10 best papers/presentations and two best exhibits at the SMTA China East 2010 Conference Award Presentation Ceremony, held on Wednesday, April 21, 2010 at the Shanghai Everbright International Hotel in conjunction with the SMTA China Annual Breakfast Reception.
Industry News | 2012-05-23 14:18:26.0
Joint Industry Guideline Provides Best Practices for Measuring the Strain on Boards and Components During Manufacturing
Technical Library | 2020-12-07 15:26:06.0
Temperature cycling testing is a method of accelerated life testing done to PCCs that are exposed to normal operation temperature variations over its lifetime. During the testing, intermittent "open" failures can first occur at the hot and cold extremes of the test, exposing weaknesses in the design and assembly. A poor/weak solder joint fatigues, a via trace or barrel cracks, loose connections or a component fails all causing an intermittent open. When not at extreme temperatures, the PCC assembly relaxes, the "open" closes creating electrical connectivity. If you are monitoring the PCC under test in-situ you will know that an intermittent failure has occurred, and the test could be stopped for inspection. If in-situ monitoring was not implemented, you would not know if there were intermittent failures or not. The PCC gets powered up and works fine at room temperature.
Technical Library | 2014-06-19 18:13:23.0
For high-density electronic packaging,the application of flip-chip solder joints has been well received in the microelectronics industry. High-lead(Pb) solders such as Sn5Pb95 are presently granted immunity from the RoHS requirements for their use in high-end flip-chip devices, especially in military applications. In flip-chip technology for consumer electronic products, organic substrates have replaced ceramic substrates due to the demand for less weight and low cost. However, the liquidus temperatures of high-Pb solders are over 300°C which would damage organic substrates during reflow because of the low glass transition temperature. To overcome this difficulty, the composite solder approach was developed...
http://www.pcb-separator.com/ https://www.pcb-separator.com/html/PRODUCTS/PCB%20separator/2019/1113/832.html Hand push pcb cutter/PCB cutting machine manufacturer/PCB V-cut machine manufacturer/PCB depaneling equipment, automatic pcb cutting machine,
http://www.pcb-separator.com/ https://www.pcb-separator.com/html/PRODUCTS/PCB%20separator/2019/1113/832.html Hand push pcb cutter/PCB cutting machine manufacturer/PCB V-cut machine manufacturer/PCB depaneling equipment, automatic pcb cutting machine,
Events Calendar | Mon Mar 16 00:00:00 EDT 2020 - Mon Mar 16 00:00:00 EDT 2020 | ,
BGA & Area Array Failures, Causes & Corrective Actions Online Webinar
SMTnet Express, October 28, 2021, Subscribers: 26,544, Companies: 11,461, Users: 26,907 Cracks: The Hidden Defect Cracks in ceramic chip capacitors can be introduced at any process step during surface mount assembly. Thermal shock
SMTnet Express, February 6, 2020, Subscribers: 33,800, Companies: 10,971, Users: 25,576 Accurately Capturing System-Level Failure of Solder Joints Credits: DfR Solutions Consortium Projects - Thermal Cycling Reliability Consortium projects allow
Heller 公司 | http://hellerindustries.com.cn/Vacuum-Void-Reduction-Reflow.pdf
]] found that the presence of a voids was not necessarily sufficient to lower solder joint reliability. Rather, the location of void relative to the solder joint failure crack path has a much larger impact than the existence of the void alone. Figure 3