Electronics Forum | Tue Aug 31 12:01:26 EDT 2004 | russ
Kris, this practice has gone on for years. I have never heard of any problems associated with this. I have heard "grumblings" about tin lead parts being processed with lead free paste, but have seen or heard of no data to support. Russ
Electronics Forum | Tue Aug 31 19:17:43 EDT 2004 | russ
Now see Dave, now I have some good info on why it is "bad", This must be the lead enrichment I have heard about but never got any substantiated data or explanantion. I wonder how much weaker or less reliable these are. Is there any data that you k
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Tue Aug 31 11:57:03 EDT 2004 | Kris
Hi Any body have any issues soldering tin lead solder paste with lead free terminations ? Components are leaded devices and chip components have read the theoritical discussions on the forum, need to know if any body has seen any real issues tod
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f
Electronics Forum | Fri Jul 06 12:11:34 EDT 2007 | james
We are starting to see issues with using Kester WS R562 with lead free components. The joints look grainy on almost all of the 0402'2 and other small components. Some of the solder does not solder to the terminations. These are hybrid boards which
Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s