| https://www.eptac.com/faqs/ask-helena-leo/ask/vapor-phase-soldering-to-immersion-tin-plated-pads
: This is a very interesting question regarding the reflow of immersion tin plating. I’ve found and attached this web site that discusses this particular issue. http://ieeexplore.ieee.org/xpl/login.jsp?tp=&arnumber=4684411&url=http%3A%2F%2Fieeexplore.ieee.org%2Fstamp%2Fstamp.jsp%3Ftp%3D%26arnumber
| https://www.eptac.com/ask/type-of-water-to-use-on-soldering-sponges/
Type of Water to Use on Soldering Sponges - EPTAC - Train. Work Smarter. Succeed Looking for solder training standards, manuals, kits, and more
| https://www.eptac.com/wp-content/uploads/2013/06/eptac_07_17_13.pdf
| https://www.eptac.com/wp-content/uploads/2021/11/eptac_07_17_13.pdf
| https://www.eptac.com/soldertip/soldertips-solderability-issues-with-nickle-plated-surfaces/
. They will re-tin with flux, but reappear following steam-aging. Is this something you have encountered before? Answer: There is a metallurgy issue with soldering to nickel plated surfaces and depending upon the thickness of the final tin/lead coating, the steam aging will penetrate the finish coating and create a
| https://www.eptac.com/faqs/soldertips/soldertip/soldertips-solderability-issues-with-nickle-plated-surfaces
. They will re-tin with flux, but reappear following steam-aging. Is this something you have encountered before? Answer: There is a metallurgy issue with soldering to nickel plated surfaces and depending upon the thickness of the final tin/lead coating, the steam aging will penetrate the finish coating and create a
| https://www.eptac.com/soldertips/soldertips-solderability-issues-with-nickle-plated-surfaces/
. They will re-tin with flux, but reappear following steam-aging. Is this something you have encountered before? Answer: There is a metallurgy issue with soldering to nickel plated surfaces and depending upon the thickness of the final tin/lead coating, the steam aging will penetrate the finish coating and create a
| https://www.eptac.com/faqs/ask-helena-leo/page/4
& Leo Have a technical question? Dealing with a process or standards issue and not sure where to turn? *Helena and Leo, our technical experts, are here to help
& Leo Have a technical question? Dealing with a process or standards issue and not sure where to turn? *Helena and Leo, our technical experts are here to help
| https://www.eptac.com/solder-tips/
? Read Answer SolderTips: Dealing with the Problems of Soldering Iron Tips Breaking Down Question: We are having a problem with soldering tips oxidizing and becoming unusable after a few hours use