Electronics Forum | Thu May 29 13:12:10 EDT 2008 | yam6rider
Just like to know what you guys thoughts regarding mixed alloys. Production run SAC305 and some components are SAC105. So, which profile should you follow. SAC105? or SAC305.
Electronics Forum | Fri Jun 06 03:28:52 EDT 2008 | reypal
I've got the same scenario. and I followed SAC105.
Electronics Forum | Wed Jul 02 08:30:32 EDT 2008 | interflux_electronics
Why not follow SAC305? you would do so for any other component finish wouldn't you? A component finish of pure Sn would also not call for a pure Sn profile, would it?
Electronics Forum | Thu Jan 29 17:04:43 EST 2009 | jeffjarmato
I run two different waves here one with SAC305 with aqueous flux the other with SN100C and No clean flux. Does anyone see any issues with running product through either machine of course after changing the Flux type? I also only use SAC305 alloy for
Electronics Forum | Tue Sep 17 15:40:59 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Tue Sep 17 15:47:04 EDT 2013 | 18424
Good day all, I wanted to get a quick poll from the folks running SAC305 in their selective soldering equipment. How are final results? How repeatable is the process, any machine related failures? pumps? nozzles? etc... I am just looking to get a
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Wed May 10 00:46:32 EDT 2006 | Chris
I agree! I am using a SAC305 no clean from Alpha. I have noticed that even hand probing with volt meter leads requires me to press very hard on the pads to bust through the flux residue.
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Thu Oct 18 11:08:22 EDT 2012 | scottp
Since we follow IPC Class III, I've done experiments turning N2 on and off and measuring void level with both SnPb and SAC305 solder. In both cases there was a statistically significant, measurable increase in voids with N2, but it wasn't significan