Electronics Forum | Sun Feb 05 09:29:12 EST 2006 | Cmiller
Look at: http://thor.inemi.org/webdownload/newsroom/Presentations/09.pdf Page 47 shows both alloys to be similar in reliability although its a little troublesome that the particular defects are not isolated as I feel there is a big difference betwee
Electronics Forum | Wed Sep 18 14:12:40 EDT 2013 | pjchonis
Hello Bachman. SAC305 is the most common lead-free solder alloy, not only for wave soldering but also selective. Most of our selective customers (especially automotive) are using SAC305. What is more important than the alloy to consider is the flux
Electronics Forum | Thu May 25 08:47:39 EDT 2006 | inds
Patrick, we were seeing a good amount of Cu-dissolution with both SAC305 and SN100C.. couldn't figure out.. till our good old vendors told us that the Cu thickness in the barrel were not correct... but anyway have started some new work with SAC30
Electronics Forum | Tue Jul 12 04:21:29 EDT 2005 | Chris Ong
Hi, Have anyone out there been using Asahi products. My knowledge is limited and I only know it from the http://www.asahisolder.com website. Pls feedback or share your view on the Asahi product. If this product worked better than other even if it h
Electronics Forum | Thu Dec 29 11:43:46 EST 2005 | samir
CMiller, Thanks for the valuable info! We are in the midst of lead-free deployment and need to know good alloy choices at both wave and ERSA. I have heard the same things regarding SAC305's price for bar solder, but don't yet know what the process
Electronics Forum | Thu May 25 19:21:58 EDT 2006 | grantp
Hi, So that's really important to have a specific flux for lead free? We are looking at changing to SN100C after reading this thread and other stuff we have found, so can anyone recommend the best no clean flux for that metal? Do you need differen
Electronics Forum | Fri Apr 04 09:54:39 EDT 2008 | redtiger56
We have been seeing continued difficulty with solder shorts and/or insufficient barrel fill with our Juki selective solder machine while using SAC305. We want to switch to something in the SN100 series, but we do not know enough to seperate the hype
Electronics Forum | Thu Jan 19 23:29:29 EST 2006 | theSaint
I've seen many comments in many threads about the positive attributes of SN100C (apparently mostly by salesmen). However, I have a concern for the higher temps that will be encountered when using SN100C (or Sn/Cu) vs. SAC305 (vs. 63/37), specifica
Electronics Forum | Tue Mar 07 14:18:32 EST 2006 | James
Billy, I have to disagree with you. We inadvertently soldered a Pb BGA with SAC305 paste and then had it micro sectioned and spectrum analyzed. Imagine our surprise when we saw the spectrum analysis showed Pb. The micro sections showed none to ac
Electronics Forum | Mon Aug 14 12:08:35 EDT 2006 | cuculi54986@yahoo.com
I agree with using the homeplate design on chips. Some Pb-free solder paste manufacturers recommend 1:1 apertures. This, in my experience, is not a good idea with any of the SAC305 pastes I've tried. I've been using the same stencil design guideli