Electronics Forum | Tue Nov 28 21:16:17 EST 2006 | davef
J Rose at EMPF says: The introduction of no-clean solder fluxes in electronics manufacturing has given rise to greater levels of solder balling simply because the opportunity to remove them in the wash process does not exist. They are typically cause
Electronics Forum | Fri Jun 19 13:40:25 EDT 1998 | Terry Burnette
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike There has been a
Electronics Forum | Fri Jun 19 14:25:24 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | There has b
Electronics Forum | Thu Jan 12 02:08:47 EST 2006 | adeline_ko
Hi, What is the different between Electroless Nickel / Immersion Gold (ENIG) and Immersion Au. Are they refer to the same finishing? We has been using the Gold thickness (0.00005 - 0.00013mm) , nicket (0.0025mm) for all Gold finishing brd (Immersio
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Wed Jun 24 16:23:29 EDT 1998 | Justin Medernach
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, Your concer
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Thu Aug 13 07:53:40 EDT 1998 | Earl Moon
| | Couple of questions. | | 1) Are we talking alumina substrates as the ceramic material? | | 2) Are we co-firing gold as the conductors on the substrate surface? | | 3) In other words, is this a hybrid thick film circuit? | | 4) If so, how large or
Electronics Forum | Thu Aug 13 03:10:22 EDT 1998 | Terry Keen
| Couple of questions. | 1) Are we talking alumina substrates as the ceramic material? | 2) Are we co-firing gold as the conductors on the substrate surface? | 3) In other words, is this a hybrid thick film circuit? | 4) If so, how large or small? S
Electronics Forum | Wed Aug 12 07:31:37 EDT 1998 | Earl Moon
| We are taking enquiries for sub-contract work that we hope to be doing by Christmas. One of the enquiries is to assemble chip capacitors and an SO14 onto ceramic. Does the printing process, paste used and reflow process remain the same, or are ther