Technical Library | 2016-01-12 11:01:25.0
More and more Land Grid Array (LGA) components are being used in electronic devices such as smartphones, tablets and computers. In order to enhance LGA mechanical strength and reliability, capillary flow underfill is used to improve reliability. However, due to the small gap, it is difficult for capillary underfill to flow into the LGA at SMT level. Due to cost considerations, there are usually no pre-heating underfill or cleaning flux residue processes at the SMT assembly line. YINCAE solder joint encapsulant SMT256 has been successfully used with solder paste for LGA assembly. Solder joint encapsulant is used in in-line LGA soldering process with enhanced reliability. It eliminates the underfilling process and provides excellent reworkability. The shear st rength of solder joint is stronger than that of underfilled components. The thermal cycling performance using solder joint encapsulant is much better than that using underfill. Bottom IC of POP has been studied for further understanding of LGA assembly process parameters. All details such as assembly process, drop test and thermal cycling test will be discussed in this paper.
Technical Library | 2020-11-24 23:01:04.0
The miniaturization trend is driving industry to adopting low standoff components or components in cavity. The cost reduction pressure is pushing telecommunication industry to combine assembly of components and electromagnetic shield in one single reflow process. As a result, the flux outgassing/drying is getting very difficult for devices due to poor venting channel. This resulted in insufficiently dried/burnt-off flux residue. For a properly formulated flux, the remaining flux activity posed no issue in a dried flux residue for no-clean process. However, when venting channel is blocked, not only solvents remain, but also activators could not be burnt off. The presence of solvents allows mobility of active ingredients and the associated corrosion, thus poses a major threat to the reliability. In this work, a new halogen-free no-clean SnAgCu solder paste, 33-76-1, has been developed. This solder paste exhibited SIR value above the IPC spec 100 MΩ without any dendrite formation, even with a wet flux residue on the comb pattern. The wet flux residue was caused by covering the comb pattern with 10 mm × 10 mm glass slide during reflow and SIR testing in order to mimic the poorly vented low standoff components. The paste 33-76-1 also showed very good SMT assembly performance, including voiding of QFN and HIP resistance. The wetting ability of paste 33-76-1 was very good under nitrogen. For air reflow, 33-76-1 still matched paste C which is widely accepted by industry for air reflow process. The above good performance on both non-corrosivity with wet flux residue and robust SMT process can only be accomplished through a breakthrough in flux technology.
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, 30 China
Phone: 0755-33578694