Electronics Forum | Wed Oct 04 10:18:51 EDT 2006 | greg york
Now seen the Blow Holes and shallow inverted and non wetting problem an aweful lot over here. Over came the Blow Holes and shallow inverted joints by washing the bare PCB with hot Saponifier then rinse and dry = problem dissapears. Think most PCB ven
Electronics Forum | Tue Aug 17 10:41:13 EDT 1999 | Steve A
Wayne, Sounds like a gasketing problem. When the horizontal apertures are bleeding but not the vertical apertures. Could be poor underside support, HASL miniscus issues, masking or plugging issues, but what many people do not account for is that t
Electronics Forum | Fri Nov 16 03:38:03 EST 2018 | premkumar_haribabu
Hi all, We have to solder a nickel tabs ( coming in SMT reels ) in to HASL PCB finish pads using refow oven & during this we facing poor wetting issues, more voids & we done pull strenth , its came out with in 1 kg ,I doubt that nickel coated materi
Electronics Forum | Tue Sep 14 14:07:45 EDT 2010 | grahamcooper22
Hi Gani, HASL is normally very good for solderability providing there is a good consistent coating of HASL on the pcb pad. But it is not unusual to have a very thin coating of HASL on the pad and this is poor for solderability. You then have tin/copp
Electronics Forum | Thu Aug 31 18:59:55 EDT 2000 | Brian W.
Our customers use OSP, HASL, immersion tin and immersion gold as board finishes. If I recommend a finish to the customer, it is one of the immersion finishes or OSP. Those finishes have the advantage of a flat surface to deposit paste. HASL has va
Electronics Forum | Tue May 09 22:57:58 EDT 2006 | davef
The NexLev connector is built in a stripline construction, providing a continuous ground plane for each signal contact. The connectors come as tenrow connectors with 100, 200, or 300 positions at possible stacking heights from 10 mm to 30 mm. Technic
Electronics Forum | Thu Apr 16 13:50:49 EDT 1998 | Lou
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X
Electronics Forum | Thu Apr 16 13:47:36 EDT 1998 | Lou
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X
Electronics Forum | Sun Nov 24 09:54:24 EST 2002 | davef
On a HASL board that has poor wetting on the pad, consider looking further downstream in the process than your assembly shop. For instance, take a look at the bare boards. Look for solder mask bleed onto the pads. This will show-up on the outside
Electronics Forum | Mon Jun 25 09:08:22 EDT 2001 | Dave G
What type of board finish ? I've seen this same defect with QFP's on some of our HASL boards. Best I can tell either the PCB's have poor solderability or uneven pad heights due to poor solder leveling at the PCB fab. Newer PCB's seem to yield bette