Electronics Forum | Mon May 17 16:34:25 EDT 2004 | pjc
I am an equip mfrs rep. I took a customer to my wave solder principal's factory to run their boards on a wave with no-Pb alloy, (Sn96.5 Ag3.0 Cu0.5) in air environment. The results were excellent with pot temp of 263C (505F). Their boards are low to
Electronics Forum | Mon Jul 26 19:37:47 EDT 2004 | Grant
Hi, It was funny. The sight of 3 men standing around the microwave daring each other to push the start button, and then freaking out when the whole thing looked as though it was going to explode was funny. I guess you have to try these things! Tho
Electronics Forum | Thu Jan 27 16:43:15 EST 2005 | russ
Ther is a solder alloy out there that is supposed to allow lead free wave processing without having to upgrade pumps and such or increasing the pot temp (direct drop in). I have not used it nor do I plan on doing leadfree wave soldering but you may
Electronics Forum | Thu May 05 03:22:38 EDT 2005 | Hannu
I do not mean big, heavy transformers but rather small ferrite core transformers, with ferrites in the range of EF16 .. EF40. The weight of the lead and its percentage of the total weight is not the issue here. We simply do not want lead-containing t
Electronics Forum | Mon May 16 18:03:30 EDT 2005 | davef
Key Issue: Will this machine solder your boards? You never know until you solder one. Any other avenues of analysis involve substantial risk. Flux Selection * High or low solids * VOC or VOC-free Solder Alloy * If using lead-free, avoid stainles
Electronics Forum | Wed May 18 14:58:05 EDT 2005 | splice
Hi, I am having some PTH non wetting issues. Setup and chronology of events is explained: Set Up; Part: 1 MM pitch connector 378 pins Solder: Kester Ultra Pure 63/37 solder Pot; 250 C pre heat; Peak 94C top side Flux: Qualitek 775, Fluxer: foam T
Electronics Forum | Thu Jul 14 04:28:45 EDT 2005 | lloyd
Folks, Thanks for all the info and suggestions but let me add a bit more to the pot. Our products work in a harsh environment and are classed as safety critical. Customer returns are our biggest concern, we don't get very many and feeling here seem
Electronics Forum | Thu Sep 01 01:21:05 EDT 2005 | cmiller
PS, sorry for any confusion, ALDSMT and CMILLER are both me. ADLSMT is my user name on SMTNET and CMILLER is me, cmiller@adltech.com I usually use cmiler to reply to stuff as if anybody e-mails me it makes more sense. adltech.com is a work in progr
Electronics Forum | Sun Sep 11 01:25:34 EDT 2005 | Mika
I agree with prior postings, but there is no perfect yes/no answers, right (left)...? Only good questions to be answered. I think it is overkill to have an extra stencil, why do you need it? (That is if you have a proper stencil cleaning equipment).
Electronics Forum | Mon Oct 03 22:16:58 EDT 2005 | Ken
If that's the case, let your customer go. I have run into this situation recently. Q. Why do you not run a dedicated line for lead free? A. You (the customer) give less than 12 weeks forcast and expect us to have a dedicated line for your product?