Electronics Forum | Wed Aug 10 21:47:17 EDT 2005 | Geoff
Nihon superior could not provide any written aprovals but In asia.......... Sony- SN100C in use for car and home audio applications. Panasonic- SN100C in use for DVD, VCR, battery, and home appliances applications. Pioneer- SN100C in use for everythi
Electronics Forum | Thu Jul 28 09:23:48 EDT 2005 | fctassembly
300 million boards to date). I also have some reliability data for joints made with these 2 alloys wave soldered and then repaired with both. All of these results look good. The issue we see is mixing SN63 with any of the lead free alloys. Sn63 wave
Electronics Forum | Thu Jul 29 21:11:13 EDT 2004 | davef
Could be lots of things. With limited information about temperatures, solder alloy, and cleaning; we'll swing for the fence that you got these solder connections very hot. So hot that Pb oxide is dominating the solder joint surface instead of the
Electronics Forum | Thu Jul 28 09:47:06 EDT 2005 | fctassembly
Hello Carl, The main reason there is little information on lead free soldering to ENIG is because most of the lead free soldering to date has been Japanese consumer products. To keep costs down, the major surface coating used has been OSP copper. It
Electronics Forum | Mon Jul 14 09:41:35 EDT 2008 | davef
Q1. Do we really need to follow the IPC J-STD-001 Solder purity? A1. Yes, you should control impurities in solder. Further information: * "Allowable concentration of contaminating elements in solder: impurities are harmless unless their level goes to
Electronics Forum | Fri Oct 23 14:20:52 EDT 2009 | waveroom
We offer SN100C solder alloys. I was asked about SN100E which is tin/copper and cobalt. Anyone know anything about the cobalt and it's pros and cons in soldering process?
Electronics Forum | Wed Jan 16 11:20:52 EST 2002 | bentzen
Hi... We tend to do a lot of footprint calculating for new SMD components. But what about the amount of solder paste on the solder pads. The amount of solder alloy is of cause determined by the stencil aperture size, stencil thickness and the sold
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Fri Jan 06 19:57:19 EST 2006 | abhinavajmera
What would be the most suitable expression for ratio of Volume of Alloy to Volume of Paste for a solder paste? For example if we use 63Sn/37Pb alloy with a 90 Wt% metal what would be an appopriate expression for the Volume Ratio?
Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (