Electronics Forum | Mon Jul 28 18:31:43 EDT 2003 | mantis
Hi There, First has the machine in question had the camera upgraded to accomdate 0603/0402. It sounds like there is a bad pickup on this part.Are all nozzles ok is feeder indexing correctly has part pick up position(Station 1) been calibrated. Hope t
Electronics Forum | Fri Aug 15 16:00:53 EDT 2003 | Cameron
Take a look at the product here: http://www.kicthermal.com/products/KIC-Auto-Focus.pdf KIC uses a previously profiled product library to calculate in spec reflow profiles for new products. Just enter you dimensions and if finds a solution for you.
Electronics Forum | Mon Oct 06 17:16:02 EDT 2003 | pjc
Yes, the OmegaMeter and IonoGraph are test equipment to measure ionic contamination. Either of those units should enable you to sort your inventory boards. for more info about this equipment, go to: www.cooksonee.com/products/scs/CoatingSystems/Ionic
Electronics Forum | Tue Apr 20 20:33:38 EDT 2004 | davef
You're correct, alcohol can cure or cause reactions in epoxies. While you're waiting for others to reply: * Read your glue supplier's application notes. They often discuss cleaning procedures and materials. * Consider searching the fine SMTnet Arch
Electronics Forum | Wed Jun 16 23:41:31 EDT 2004 | rodionp
ricardof Unfortunately I cannot comment on many of your questions however I can lead you to one important article as to basic assembly optimization techniques to maximise throughput (or minimize assembly time, which is pretty much the same thing...)
Electronics Forum | Fri Aug 06 07:16:36 EDT 2004 | davef
When moisture outgasses through plating, it continues through the molten solder, causing a meak solder connection. There's another issue with thin plating that we haven't focused on in this thread. If plating is thin, the stress on the barrel of a
Electronics Forum | Tue Sep 14 10:24:53 EDT 2004 | pjc
MPM is a printing machine design and mfg company based in Franklin MA USA. Printing machines are used to deposit hi viscosity materials such as solderpaste, adhesives and silver epoxy used by the electronics assembly and semi-conductor industry. The
Electronics Forum | Thu Sep 30 08:08:50 EDT 2004 | davef
Habba: Here is a thread from the fine SMTnet Archives from a couple of weeks ago, where we spoke about the topic of mixed lead-free solder with components that have lead-bearing solderability protection: http://www.smtnet.com/forums/Index.cfm?CFApp=
Electronics Forum | Mon Nov 01 09:44:38 EST 2004 | M Cyr
Hi Chez, If you are still in need of support, you may locate Universal support information at here: http://www.uic.com/wcms/WCMS2.nsf/index/Contact_Us_94.html You should start with IM technical support. Depending upon the assessment, they may recomm
Electronics Forum | Thu Oct 21 17:05:11 EDT 2004 | davef
While it's not exactly what you asked, it's similar. Here is a thread from the fine SMTnet Archives from a couple of weeks ago, where we spoke about the topic of mixed lead-free solder with components that have lead-bearing solderability protection: