Electronics Forum | Mon Sep 18 19:58:10 EDT 2000 | Dave F
broad answer. There's tons of suppliers. Go to "Circuit Assembly" magazine web site and look-up flux suppliers in the "Buyers Guide." Broad line suppliers are Kester, Alpha ... They will make you answer: I'm joining bla, bla, bla metals, using b
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (
Electronics Forum | Thu Nov 17 20:51:16 EST 2005 | cangly
Morning Mike, We use Pb63/Sn37, Alpha Metal alloy. Solder pot is at 250 C. The profile of board after Preheat about 100 C, Lambda Wave about 220C (use both Lambda and Chip wave), DWell time 2.1s ~ 3s. Conveyor speed 1.5 in/min. We run by bare board a
Electronics Forum | Thu Nov 17 03:34:51 EST 2005 | cangly
Hi, We have a board with over 100 chips (mixed size) and some long Connector DIP through out Wave solder with many issues of no solder and solder bridge, (using clean flux with bubble fluxer and Kester solder bar). Currently we tried to reduce the de
Electronics Forum | Thu Nov 17 08:57:39 EST 2005 | russ
No clean and foam fluxing is not a very good process from my experience. I know that the flux manufacturers claim that they are suitable but I am not sure what "suitable" means. I would bet that you have very inconsistant flux coverage. How often
Electronics Forum | Thu Nov 17 21:46:48 EST 2005 | C. Kolokoy
With DIP type components, a sub-par fluxing method (foaming a no-clean), and a chip wave where one is not needed are formulas for bridging and insufficient wetting. If you have SMD's on the wave solder side of the board greater than 0603, and no SOT
Electronics Forum | Tue Dec 03 11:59:01 EST 2002 | slthomas
We haven't run a profile yet....probably because we're a-feared to. We can't do topside preheating here to any degree because we use an aluminum plate for aligning hundreds of top side through-hole components (pots, switches, buttons, LEDs) that te
Electronics Forum | Tue Aug 26 13:44:14 EDT 2008 | cgray
The chain and fingers for our Wave solder is getting a large amount of residue from the flux (high dissolved solids) we are using. Any recommendations for products that can clean polymerized flux.